Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238 | 2.0 | g/10min |
| Density / Specific Gravity | | ASTMD1505 | 0.920 | g/cm³ |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ASTMD1525 | 93.0 | °C |
| Brittleness Temperature | | ASTMD746 | -70.0 | °C |
| Melting temperature | | | 122 | °C |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|
| Film Thickness - Tested) | | | 38 | µm |
| Secant Modulus | 1%正割,MD:38µm,吹塑薄膜 | ASTMD882 | 147 | Mpa |
| Secant Modulus | 1%正割,TD:38µm,吹塑薄膜 | ASTMD882 | 206 | Mpa |
| Tensile Elongation | MD:断裂,38µm,吹塑薄膜 | ASTMD882 | 600 | % |
| Tensile Elongation | TD:断裂,38µm,吹塑薄膜 | ASTMD882 | 800 | % |
| Elmendorf Tear Strength | MD:38µm,吹塑薄膜 | ASTMD1922 | 61 | g |
| Elmendorf Tear Strength | TD:38µm,吹塑薄膜 | ASTMD1922 | 650 | g |
| Tensile Strength | MD:屈服,38µm,吹塑薄膜 | ASTMD882 | 9.81 | Mpa |
| Tensile Strength | TD:屈服,38µm,吹塑薄膜 | ASTMD882 | 10.8 | Mpa |
| Tensile Strength | MD:断裂,38µm,吹塑薄膜 | ASTMD882 | 35.3 | Mpa |
| Tensile Strength | TD:断裂,38µm,吹塑薄膜 | ASTMD882 | 27.5 | Mpa |
| Gardner Impact | 38µm,吹塑薄膜 | ASTMD1709 | 120 | g |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Haze | 38.0µm,吹塑薄膜 | ASTMD1003 | 24 | % |
| Gloss | 45°,38.0µm,吹塑薄膜 | ASTMD2457 | 47 | |
| Transmittance | | ASTMD1746 | 53.0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.