Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | | ASTM D-955 | 0.4 | % |
| Shrinkage rate | MD | ASTMD955 | <0.40 | % |
| Water absorption rate | 24hr | ASTMD570 | <0.30 | % |
| Melt mass flow rate | 200°C/5.0kg | ASTMD1238 | 0.80 | g/10min |
| Melt mass flow rate | 220°C/10.0kg | ASTMD1238 | 8.0 | g/10min |
| Density/specific gravity | | ASTMD792 | 1.03 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending strength 4 | 屈服,23°C | ASTMD790 | 58.6 | Mpa |
| Tensile strength at the point of surrender | 23℃ | ASTM D-638 | 350 | kg/cm |
| Tensile strength at the point of surrender | 23℃ | ASTM D-638 | 5000 | psi |
| Bending modulus 3 | 23°C | ASTMD790 | 2000 | Mpa |
| Tensile strength at fracture point | 1/8" | ASTM D-638 | 4300 | kg/cm |
| Tensile strength at fracture point | 1/8" | ASTM D-638 | 300 | psi |
| Tensile strength 2 | 屈服,23°C,3.18mm | ASTMD638 | 32.4 | Mpa |
| Elongation rate 2 | 断裂,23°C,3.18mm | ASTMD638 | 90 | % |
| Tensile strength 2 | Break,23°C,3.18mm | ASTMD638 | 27.6 | Mpa |
| Flexural coefficient | 23℃ 2.8mm/min | ASTM D-790 | 20000 | kg/cm |
| Flexural coefficient | 23℃ 2.8mm/min | ASTM D-790 | 290000 | psi |
| IZOD notch impact strength | 23℃1/2" | ASTM D-256 | 38 (7.0) | kg.cm/cm(ft.1b/in) |
| IZOD notch impact strength | 23℃1/8" | ASTM D-256 | 53 (9.8) | kg.cm/cm(ft.1b/in) |
| Flexural strength | 23℃ 2.8mm/min | ASTM D-790 | 600 | kg/cm |
| Flexural strength | 23℃ 2.8mm/min | ASTM D-790 | 8500 | psi |
| elongation at break | 1/8" | ASTM D-638 | 50 | % |
| Rockwell hardness | | | 100 | |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 未退火 | ASTM D-1525 | 85(185) | ℃(F) |
| Hot deformation temperature | 1.8MPa,未退火,12.7mm | ASTMD648 | 85.0 | °C |
| vicat softening point | | ASTM D-1525 | 100 | °C |
| Vicat softening temperature | | ASTMD15254 | 102 | °C |
| Flame retardant grade | | UL94 | HB | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTMD256 | 450 | J/m |
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTMD256 | 490 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R计秤,23°C | ASTMD785 | 100 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| FlameRating | 1.6mm | UL94 | HB | |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | | ASTM D-792 | 1.03 | |
| Water absorption rate | | ASTM D-570 | 0.3 | wt% |
| Melt index | 200℃/5kg | ASTM D-1238 | 0.8 | g/10min |
| Melt index | 200℃/5kg | ASTM D-1238 | 8.0 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.