Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 3100 TAIDA TAIWAN
TAITALAC®
Helmet、Low temperature products、Toolbox、Bus box、Locomotive parts、Application in the automo、heel、Footwear、Controlled pipe fittings,、Used for luggage
Excellent hot forming、Ultra high impact resista、Widely used for extrusion、Ultra high impact strengt、Good processability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ABS/TAIDA TAIWAN/3100
Density/specific gravity
ASTMD792
g/cm³
1
Melt mass flow rate
200°C/5.0kg
ASTMD1238
g/10min
0
Melt mass flow rate
220°C/10.0kg
ASTMD1238
g/10min
8
Shrinkage rate
MD
ASTMD955
%
<
Shrinkage rate
ASTM D-955
%
0
Water absorption rate
24hr
ASTMD570
%
<
Mechanical performance
Test Condition
Test Method
Unit
ABS/TAIDA TAIWAN/3100
IZOD notch impact strength
23℃1/2"
ASTM D-256
kg.cm/cm(ft.1b/in)
3
IZOD notch impact strength
23℃1/8"
ASTM D-256
kg.cm/cm(ft.1b/in)
5
Tensile strength at fracture point
1/8"
ASTM D-638
kg/cm
4
Tensile strength at fracture point
1/8"
ASTM D-638
psi
3
elongation at break
1/8"
ASTM D-638
%
5
Tensile strength at the point of surrender
23℃
ASTM D-638
kg/cm
3
Tensile strength at the point of surrender
23℃
ASTM D-638
psi
5
Tensile strength 2
屈服,23°C,3.18mm
ASTMD638
Mpa
3
Flexural strength
23℃ 2.8mm/min
ASTM D-790
kg/cm
6
Flexural strength
23℃ 2.8mm/min
ASTM D-790
psi
8
Flexural coefficient
23℃ 2.8mm/min
ASTM D-790
kg/cm
2
Flexural coefficient
23℃ 2.8mm/min
ASTM D-790
psi
2
Tensile strength 2
Break,23°C,3.18mm
ASTMD638
Mpa
2
Elongation rate 2
断裂,23°C,3.18mm
ASTMD638
%
9
Bending modulus 3
23°C
ASTMD790
Mpa
2
Bending strength 4
屈服,23°C
ASTMD790
Mpa
5
Thermal performance
Test Condition
Test Method
Unit
ABS/TAIDA TAIWAN/3100
Hot deformation temperature
1.8MPa,未退火,12.7mm
ASTMD648
°C
8
Hot deformation temperature
未退火
ASTM D-1525
℃(F)
8
vicat softening point
ASTM D-1525
°C
1
Vicat softening temperature
ASTMD15254
°C
1
Impact performance
Test Condition
Test Method
Unit
ABS/TAIDA TAIWAN/3100
Impact strength of cantilever beam gap
23°C,6.35mm
ASTMD256
J/m
4
Impact strength of cantilever beam gap
23°C,3.18mm
ASTMD256
J/m
4
Basic performance
Test Condition
Test Method
Unit
ABS/TAIDA TAIWAN/3100
Melt index
200℃/5kg
ASTM D-1238
g/10min
0
Melt index
200℃/5kg
ASTM D-1238
g/10min
8
Water absorption rate
ASTM D-570
wt%
0