Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.14 | |
| Water absorption rate 23 ℃/24h | | ASTM D570/ISO 62 | 2.5 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD2.0mm | ASTMD995 | 1.3 | % |
| Shrinkage rate | TD2.0mm | ASTMD995 | 2.0 | % |
| Water absorption rate | (23°C,24hr) | ASTMD570 | 2.5 | % |
| Shrinkage rate | 干 | 旭化成方法 | 1.3-2.0 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Cantilever beam notch impact strength | 干(湿) | ASTM D-256 | 39(147) | J/m |
| tensile strength | 干(湿) | ASTM D-638 | 79(57) | Mpa |
| Fracture elongation rate | 干(湿) | ASTM D-638 | 50(250) | % |
| Rockwell hardness | 干(湿) | ASTM D-785 | 120(108) | R scale |
| Flexural strength | 干(湿) | ASTM D-790 | 118(54) | Mpa |
| Scratch resistance coefficient | 干(湿) | ASTM D-790 | 2.8(1.2) | GPa |
| Wear rate | 湿 | ASTM D-1044 | 7 | |
| elongation at break | 23°C | ASTMD638 | 50 | % |
| bending strength | 23°C | ASTMD790 | 118 | Mpa |
| Bending modulus | 23°C | ASTMD790 | 2800 | Mpa |
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 39 | J/m |
| elongation at break | | ASTM D638/ISO 527 | 50 | % |
| Bending modulus | | ASTM D790/ISO 178 | 2790 | kg·cm/cm(J/M)ft·lb/in |
| bending strength | | ASTM D790/ISO 178 | 118 | kg·cm/cm(J/M)ft·lb/in |
| Rockwell hardness | 干(湿) | ASTM D-785 | 80(55) | M Scale |
| tensile strength | 23°C | ASTMD638 | 79 | Mpa |
| Charpy impact strength | | ASTM D256/ISO 179 | 39 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.46MPa,干 | ASTM D-648 | 230 | °C |
| Hot deformation temperature | 1.82MPa,干 | ASTM D-648 | 70 | °C |
| Flame retardancy | 干 | UL 94 | V-2 | |
| Linear expansion coefficient | 干 | ASTM D-696 | 8 | |
| Thermal conductivity | 干 | | 0.2 | W/(m.K) |
| Specific heat capacity | 干 | | 1670 | J/(kg.k) |
| Combustibility (rate) | | UL94 | v-2 | |
| Hot deformation temperature | | ASTM D648/ISO 75 | 230 | ℃（℉） |
| Linear expansion coefficient | | ASTM D696/ISO 11359 | 8 | mm/mm.℃ |
| Hot deformation temperature | 0.45MPa未退火 | ASTMD648 | 230 | °C |
| Hot deformation temperature | 1.80MPa未退火 | ASTMD648 | 70 | °C |
| Coefficient of linear expansion | 导热系数 | JISR2618 | 0.2 | W/m/K |
| Coefficient of linear expansion | 比热 | | 1670 | J/kg/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Insulation strength | | ASTMD149 | 20 | KV/mm |
| Dissipation factor | 相对漏电起痕指数 | ASTMD3638 | 600 | V |
| Volume resistivity | | ASTM D257/IEC 60093 | 10-10 | Ω.cm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | | ASTMD785 | 80 | M（Scale） |
| Rockwell hardness | | ASTMD785 | 120 | R |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Fire rating | | UL-94 | 0.40mm | V-2 |
| Fire rating | | UL-94 | 0.71mm | V-2 |
| Fire rating | | UL-94 | 1.50mm | V-2 |
| Fire rating | | UL-94 | 3.00mm | V-2 |
| Fire rating | 氧指数 | ASTM2863 | 26 | % |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture absorption rate | 湿 | | 2.5 | % |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Oxygen index | 干 | ASTM D-2863 | 26 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.