PA66 1300S ASAHI JAPAN
Leona™
Connector、parts、Automotive sector、Consumer goods sector
High mobility、High rigidity、Good flexibility
UL
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/1300S
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
2
physical property
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/1300S
Shrinkage rate
干
旭化成方法
%
1
Shrinkage rate
MD2.0mm
ASTMD995
%
1
Shrinkage rate
TD2.0mm
ASTMD995
%
2
Water absorption rate
(23°C,24hr)
ASTMD570
%
2
Mechanical performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/1300S
elongation at break
23°C
ASTMD638
%
5
elongation at break
ASTM D638/ISO 527
%
5
Fracture elongation rate
干(湿)
ASTM D-638
%
5
Flexural strength
干(湿)
ASTM D-790
Mpa
1
Scratch resistance coefficient
干(湿)
ASTM D-790
GPa
2
tensile strength
干(湿)
ASTM D-638
Mpa
7
tensile strength
23°C
ASTMD638
Mpa
7
Rockwell hardness
干(湿)
ASTM D-785
R scale
1
Rockwell hardness
干(湿)
ASTM D-785
M Scale
8
Bending modulus
23°C
ASTMD790
Mpa
2
Bending modulus
ASTM D790/ISO 178
kg·cm/cm(J/M)ft·lb/in
2
bending strength
ASTM D790/ISO 178
kg·cm/cm(J/M)ft·lb/in
1
bending strength
23°C
ASTMD790
Mpa
1
Impact strength of cantilever beam gap
23°C
ASTMD256
J/m
3
Cantilever beam notch impact strength
干(湿)
ASTM D-256
J/m
3
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
3
Thermal performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/1300S
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
2
Hot deformation temperature
0.46MPa,干
ASTM D-648
°C
2
Hot deformation temperature
1.82MPa,干
ASTM D-648
°C
7
Hot deformation temperature
0.45MPa未退火
ASTMD648
°C
2
Hot deformation temperature
1.80MPa未退火
ASTMD648
°C
7
Coefficient of linear expansion
导热系数
JISR2618
W/m/K
0
Linear expansion coefficient
ASTM D696/ISO 11359
mm/mm.℃
8
Electrical performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/1300S
Dissipation factor
相对漏电起痕指数
ASTMD3638
V
6
Insulation strength
ASTMD149
KV/mm
2
Volume resistivity
ASTM D257/IEC 60093
Ω.cm
1
hardness
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/1300S
Rockwell hardness
ASTMD785
M（Scale）
8
Rockwell hardness
ASTMD785
R
1
flammability
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/1300S
Fire rating
UL-94
V-2
0
Fire rating
UL-94
V-2
0
Fire rating
UL-94
V-2
1
Fire rating
UL-94
V-2
3
Fire rating
氧指数
ASTM2863
%
2
Other performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/1300S
Oxygen index
干
ASTM D-2863
%
2