ASA KIBILAC® PW-957 TAIWAN CHIMEI
714
- Properties:High glossHigh mobilityWeather resistance
- Usages:Electrical toolsElectrical fieldElectrical appliancesElectronic fieldAutomotive sectorLighting fixtures
- Certificates:MSDSRoHSULTDSTDSULMSDSRoHSSVHCProcessing物质宣告书
Compare
View PricesTechnical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.07 | ||
| Melt index (flow coefficient) | ASTM D1238/ISO 1133 | 28 | g/10min |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 220°C/10.0kg | ASTMD1238 | 23 | g/10min |
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 23.0 | cm3/10min |
| Shrinkage rate | ISO294-4 | 0.40to0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength 3 | 屈服 | ASTMD638 | 43.0 | Mpa |
| Tensile stress | 屈服 | ISO527-2/50 | 46.0 | Mpa |
| 断裂 | ISO527-2/50 | 33.0 | Mpa | |
| Elongation rate 4 | 断裂 | ASTMD638 | 55 | % |
| Tensile strain | 断裂 | ISO527-2/50 | 20 | % |
| Bending modulus 4 | ASTMD790 | 2160 | Mpa | |
| tensile strength | ASTM D638/ISO 527 | 440 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 650 | kg/cm²(MPa)[Lb/in²] | |
| Tensile strength | ASTM D-638 | 420 | kg/cm | |
| bending strength | ASTM D-790 | 550 | kg/cm | |
| Bending modulus 5 | ISO178 | 2200 | Mpa | |
| Bending strength 4 | ASTMD790 | 63.3 | Mpa | |
| Bending stress 5 | ISO178 | 67.0 | Mpa | |
| IZOD impact strength | 1/8" | ASTM D-256 | 15 | kg.cm/cm |
| IZOD notch impact strength | ASTM D256/ISO 179 | 10 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 15 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | ASTM D648/ISO 75 | 95 | ℃（℉） | |
| ASTM D648/ISO 75 | 85 | ℃（℉） | ||
| vicat softening point | ASTM D1525/ISO R306 | 105 | ℃（℉） | |
| softening point | ASTM D-1525 | 105 | °C | |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 80.0 | °C |
| 1.8MPa,退火 | ISO75-2/A | 97.0 | °C | |
| Vicat softening temperature | ASTMD15256 | 105 | °C | |
| -- | ISO306/A50 | 105 | °C | |
| -- | ISO306/B50 | 94.0 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 9E-05 | cm/cm/°C |
| Hot deformation temperature | Annealed | ASTMD648 | 95 | °C |
| Unannealed | ASTMD648 | 85 | °C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R级 | ASTMD785 | 105 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | 220℃,10kg | ASTM D-1238 | 28 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.