ASA KIBILAC® PW-957 TAIWAN CHIMEI
257
- Unit Price:
- $2343 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 375MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High gloss High mobility Weather resistance
- Application Areas:packing Electrical field Electrical appliances Electronic field Automotive sector Charger casing
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.07 | ||
| Melt index (flow coefficient) | ASTM D1238/ISO 1133 | 28 | g/10min |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | ISO294-4 | 0.40to0.70 | % | |
| Melt mass flow rate | 220°C/10.0kg | ASTMD1238 | 23 | g/10min |
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 23.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength 3 | Yield | ASTMD638 | 43.0 | Mpa |
| Bending modulus 4 | ASTMD790 | 2160 | Mpa | |
| Bending strength 4 | ASTMD790 | 63.3 | Mpa | |
| Tensile strength | ASTM D-638 | 420 | kg/cm | |
| Elongation rate 4 | Break | ASTMD638 | 55 | % |
| Bending modulus 5 | ISO178 | 2200 | Mpa | |
| Bending stress 5 | ISO178 | 67.0 | Mpa | |
| Tensile stress | Yield | ISO527-2/50 | 46.0 | Mpa |
| Break | ISO527-2/50 | 33.0 | Mpa | |
| Tensile strain | Break | ISO527-2/50 | 20 | % |
| tensile strength | ASTM D638/ISO 527 | 440 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 650 | kg/cm²(MPa)[Lb/in²] | |
| ASTM D-790 | 550 | kg/cm | ||
| IZOD impact strength | 1/8" | ASTM D-256 | 15 | kg.cm/cm |
| IZOD notch impact strength | ASTM D256/ISO 179 | 10 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 15 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| softening point | ASTM D-1525 | 105 | °C | |
| Vicat softening temperature | ASTMD15256 | 105 | °C | |
| -- | ISO306/A50 | 105 | °C | |
| -- | ISO306/B50 | 94.0 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 9E-05 | cm/cm/°C |
| Hot deformation temperature | ASTM D648/ISO 75 | 95 | ℃（℉） | |
| ASTM D648/ISO 75 | 85 | ℃（℉） | ||
| 1.8MPa,Unannealed | ISO75-2/A | 80.0 | °C | |
| 1.8MPa,Annealed | ISO75-2/A | 97.0 | °C | |
| Annealed | ASTMD648 | 95 | °C | |
| Unannealed | ASTMD648 | 85 | °C | |
| vicat softening point | ASTM D1525/ISO R306 | 105 | ℃（℉） |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTMD785 | 105 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | 220℃,10kg | ASTM D-1238 | 28 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.