Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.2 | |
| Molding shrinkage rate | | ASTM D955 | 0.5-0.7 | % |
| Water absorption rate 23 ℃/24h | | ASTM D570/ISO 62 | 0.23 | % |
| Melt index (flow coefficient) | | ASTM D1238/ISO 1133 | 12 cm3/10min(300℃/1.2kg ) | g/10min |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Light transmittance | | | 85～89 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| elongation at break | | ASTM D638/ISO 527 | tB 90 | % |
| tensile strength | | ASTM D638/ISO 527 | Y 65 | kg/cm²(MPa)[Lb/in²] |
| Rockwell hardness | | ASTM D785 | R120,M50 | |
| Bending modulus | | ASTM D790/ISO 178 | 2.3(GPa) | kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 90 | kg/cm²(MPa)[Lb/in²] |
| Flexural modulus of elasticity | | | 2350 | Mpa |
| Flexural strength | | | 93 | Mpa |
| Rockwell hardness | | | R120（M75） | |
| Tensile strength | | | 68 | Mpa |
| Destructive elongation rate | | | 115 | % |
| Tensile yield strength | | | 64 | Mpa |
| sliding friction | | | 12 | |
| Tensile modulus of elasticity | | | 2300 | Mpa |
| IZOD impact strength | 3.2mm | | 90 | KJ/m |
| IZOD impact strength | 4mm | | 70 | KJ/m |
| IZOD notch impact strength | | ASTM D256/ISO 179 | 80 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Combustibility | 3mm | | V-0 | |
| Combustibility (rate) | | UL94 | V0/3.0mm | |
| vicat softening point | | | 148 | °C |
| Linear expansion coefficient | | ASTM D696/ISO 11359 | 6.5 | mm/mm.℃ |
| Load deflection temperature | | | 148 | °C |
| Coefficient of linear expansion | | | 6.5 | |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Insulation breakdown voltage | | | 30 | KV/mm |
| dielectric loss tangent | 1MHz | | 9.2×10 | |
| dielectric loss tangent | 60Hz | | 6.6×10 | |
| Volume intrinsic resistance | | | ＜10 | Ω.m |
| Capacitance rate | 1MHz | | 2.85 | |
| Capacitance rate | 60Hz | | 2.91 | |
| Dielectric constant | | ASTM D150/IEC 60250 | 2.85 | |
| Arc resistance | | | 110 | sec |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | | | 0.5～0.7% | % |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | | | 0.23 | % |
| Melt index | | | 12 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.