PC TARFLON™ IRY2200 IDEMITSU JAPAN
211
- Unit Price:
- $3259 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 25MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:transparent Flame retardant High temperature resistan Low viscosity
- Application Areas:currency
- Color:--
- Grade:Weather resistant grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.2 | ||
| Molding shrinkage rate | ASTM D955 | 0.5-0.7 | % | |
| Melt index (flow coefficient) | ASTM D1238/ISO 1133 | 12 cm3/10min(300℃/1.2kg ) | g/10min | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.23 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Light transmittance | 85～89 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| elongation at break | ASTM D638/ISO 527 | tB 90 | % | |
| tensile strength | ASTM D638/ISO 527 | Y 65 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | R120,M50 | ||
| Bending modulus | ASTM D790/ISO 178 | 2.3(GPa) | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 90 | kg/cm²(MPa)[Lb/in²] | |
| Destructive elongation rate | 115 | % | ||
| Flexural modulus of elasticity | 2350 | Mpa | ||
| Tensile yield strength | 64 | Mpa | ||
| sliding friction | 12 | |||
| Tensile strength | 68 | Mpa | ||
| Tensile modulus of elasticity | 2300 | Mpa | ||
| Flexural strength | 93 | Mpa | ||
| Rockwell hardness | R120（M75） | |||
| IZOD impact strength | 4mm | 70 | KJ/m | |
| 3.2mm | 90 | KJ/m | ||
| IZOD notch impact strength | ASTM D256/ISO 179 | 80 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility | 3mm | V-0 | ||
| Combustibility (rate) | UL94 | V0/3.0mm | ||
| Linear expansion coefficient | ASTM D696/ISO 11359 | 6.5 | mm/mm.℃ | |
| Load deflection temperature | 148 | °C | ||
| vicat softening point | 148 | °C | ||
| Coefficient of linear expansion | 6.5 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric constant | ASTM D150/IEC 60250 | 2.85 | ||
| Arc resistance | 110 | sec | ||
| Capacitance rate | 60Hz | 2.91 | ||
| Volume intrinsic resistance | ＜10 | Ω.m | ||
| Capacitance rate | 1MHz | 2.85 | ||
| dielectric loss tangent | 1MHz | 9.2×10 | ||
| 60Hz | 6.6×10 | |||
| Insulation breakdown voltage | 30 | KV/mm |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | 0.5～0.7% | % |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | 12 | g/10min | ||
| Water absorption rate | 0.23 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.