Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238 | 1.8 | g/10min |
| Vinyl acetate content | | | 18.0 | wt% |
| Density/specific gravity | | ASTMD1505 | 0.938 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| elongation | 断裂 | ASTMD638 | 800 | % |
| Bending modulus | | ASTMD790 | 39.2 | Mpa |
| Tensile strength | 屈服 | ASTMD638 | 4.41 | Mpa |
| Tensile strength | 断裂 | ASTMD638 | 14.7 | Mpa |
| friction coefficient | 吹塑薄膜 | ASTMD1894 | 0.50 | |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | | ASTMD1525 | 60.0 | °C |
| Brittle temperature | | ASTMD746 | -70.0 | °C |
| Melting temperature | | | 84.0 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|
| Film thickness - tested | | | 30 | µm |
| Secant modulus | 1%正割,MD:30µm,吹塑薄膜 | ASTMD882 | 34.3 | Mpa |
| Secant modulus | 1%正割,TD:30µm,吹塑薄膜 | ASTMD882 | 37.3 | Mpa |
| elongation | MD:断裂,30µm,吹塑薄膜 | ASTMD882 | 500 | % |
| elongation | TD:断裂,30µm,吹塑薄膜 | ASTMD882 | 600 | % |
| Elmondov tear strength | MD:30µm,吹塑薄膜 | ASTMD1922 | 12 | g |
| Elmondov tear strength | TD:30µm,吹塑薄膜 | ASTMD1922 | 29 | g |
| Tensile strength | MD:屈服,30µm,吹塑薄膜 | ASTMD882 | 3.92 | Mpa |
| Tensile strength | TD:屈服,30µm,吹塑薄膜 | ASTMD882 | 2.94 | Mpa |
| Tensile strength | MD:断裂,30µm,吹塑薄膜 | ASTMD882 | 27.5 | Mpa |
| Tensile strength | TD:断裂,30µm,吹塑薄膜 | ASTMD882 | 24.5 | Mpa |
| Falling hammer impact | 30µm,吹塑薄膜 | ASTMD1709 | 650 | g |
| Available film thickness | | | 1.2-5.9mil(30-150µ | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore hardness | 邵氏A | ASTMD2240 | 8838 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| gloss | 45°,30.0µm,吹塑薄膜 | ASTMD2457 | 90 | |
| Haze | 30.0µm,吹塑薄膜 | ASTMD1003 | 3.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.