Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate 23 ℃/24h | | ASTM D570/ISO 62 | 1.8 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | TD | ISO294-4 | 0.60 | % |
| Shrinkage rate | MD | ISO294-4 | 0.20 | % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 6.3 | % |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO62 | 1.9 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | 断裂 | ISO527-2 | 180 | Mpa |
| Tensile strain | 断裂 | ISO527-2 | 3.5 | % |
| Tensile modulus | | ASTM D638/ISO 527 | 9100 | kg/cm²(MPa)[Lb/in²] |
| Tensile modulus | | ISO527-2 | 10000 | Mpa |
| Bending modulus | | ISO178 | 8500 | Mpa |
| Bending modulus | | ASTM D790/ISO 178 | 9000 | kg/cm²(MPa)[Lb/in²] |
| Compressive stress | | ISO604 | 160 | Mpa |
| shear strength | | ASTMD732 | 60.0 | Mpa |
| Bending stress | | ISO178 | 240 | Mpa |
| Charpy impact strength | | ASTM D256/ISO 179 | 6 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.4E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO11359-2 | 1E-04 | cm/cm/°C |
| Melting temperature 2 | | ISO11357-3 | 221 | °C |
| Hot deformation temperature | | ASTM D648/ISO 75 | 221 | ℃（℉） |
| Hot deformation temperature | | ASTM D648/ISO 75 | 210 | ℃（℉） |
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 220 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 210 | °C |
| melting point | | | 221 | ℃（℉） |
| vicat softening point | | ASTM D1525/ISO R306 | 215 | ℃（℉） |
| Glass transition temperature 2 | | ISO11357-2 | 60.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation factor | 100Hz | IEC60250 | 0.022 | |
| Relative permittivity | 100Hz | IEC60250 | 3.80 | |
| Leakage Trace Index | | IEC60112 | 600 | V |
| Compared to the anti leakage trace index | CTI | UL746 | PLC0 | |
| Volume resistivity | | IEC60093 | 1E+14 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 80 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 90 | kJ/m² |
| Unscented Izod impact strength | -30°C | ISO180/1U | 90 | kJ/m² |
| Unscented Izod impact strength | 23°C | ISO180/1U | 100 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| UL flame retardant rating | 3.0mm | UL94 | HB | |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
| UL flame retardant rating | 3.0mm | IEC60695-11-10,-20 | HB | |
| Extreme Oxygen Index | | ISO4589-2 | 21 | % |
| FMVSS flammability | | FMVSS302 | B | |
| atomization | F-value(refraction) | ISO6452 | 95 | % |
| atomization | G-value(condensate) | ISO6452 | 1E-04 | g |
| Burning rate 3 | 1.00mm | ISO3795 | 25 | mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| EmissionofOrganicCompounds | | VDA277 | 8.50 | µgC/g |
| Odor | | VDA270 | 3.50 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.