PA6 Zytel® 73G30L NC010 DUPONT USA

182

Unit Price:
$1620 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
82MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High temperature resistan enhance
Application Areas:auto parts Electronic appliances Home appliance accessorie
Color:--
Grade:Injection grade

Technical Data Sheet Compare

Physical properties	Test Condition	Test Method	Test Result	Unit
Water absorption rate 23 ℃/24h		ASTM D570/ISO 62	1.8	%

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD	ISO294-4	0.60	%
Shrinkage rate	Shrinkage rate	MD	ISO294-4	0.20	%
Water absorption rate	Saturation,23°C,2.00mm	ISO62	6.3	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO62	1.9	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ISO527-2	10000	Mpa
Tensile stress	Break	ISO527-2	180	Mpa
Tensile strain	Break	ISO527-2	3.5	%
Bending modulus		ISO178	8500	Mpa
Bending stress		ISO178	240	Mpa
Compressive stress		ISO604	160	Mpa
shear strength		ASTMD732	60.0	Mpa
Tensile modulus		ASTM D638/ISO 527	9100	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	9000	kg/cm²(MPa)[Lb/in²]
Charpy impact strength		ASTM D256/ISO 179	6	kg·cm/cm(J/M)ft·lb/in

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature		ASTM D648/ISO 75	221	℃（℉）
Hot deformation temperature	Hot deformation temperature		ASTM D648/ISO 75	210	℃（℉）
melting point			221	℃（℉）
vicat softening point		ASTM D1525/ISO R306	215	℃（℉）
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	220	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	210	°C
Glass transition temperature 2		ISO11357-2	60.0	°C
Melting temperature 2		ISO11357-3	221	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	1.4E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	1E-04	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		IEC60093	1E+14	ohms·cm
Relative permittivity	100Hz	IEC60250	3.80
Dissipation factor	100Hz	IEC60250	0.022
Compared to the anti leakage trace index	CTI	UL746	PLC0
Leakage Trace Index		IEC60112	600	V

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	80	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	90	kJ/m²
Unscented Izod impact strength	-30°C	ISO180/1U	90	kJ/m²
Unscented Izod impact strength	Unscented Izod impact strength	23°C	ISO180/1U	100	kJ/m²

flammability	Test Condition	Test Method	Test Result	Unit
Burning rate 3	1.00mm	ISO3795	25	mm/min
UL flame retardant rating	1.5mm	UL94	HB
	UL flame retardant rating	3.0mm	UL94	HB
		UL flame retardant rating	1.5mm	IEC60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	3.0mm	IEC60695-11-10,-20	HB
Extreme Oxygen Index		ISO4589-2	21	%
FMVSS flammability		FMVSS302	B
atomization	F-value(refraction)	ISO6452	95	%
atomization	atomization	G-value(condensate)	ISO6452	1E-04	g

Supplementary Information	Test Condition	Test Method	Test Result	Unit
EmissionofOrganicCompounds		VDA277	8.50	µgC/g
Odor		VDA270	3.50

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.