EAA PRIMACOR™ 1410 STYRON US
709
- Properties:High toughnessHeat sealing performancehigh strength
- Usages:film
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238,ISO1133 | 1.5 | g/10min |
| Content of comonomer 3 | 内部方法 | 9.7 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | 屈服,模压成型4 | ASTMD638 | 8.39 | Mpa |
| 屈服,模压成型 | ISO527-2/508 | 8.39 | Mpa | |
| 断裂,模压成型4 | ASTMD638 | 22.5 | Mpa | |
| 断裂,模压成型 | ISO527-2/508 | 22.5 | Mpa | |
| elongation | 断裂,模压成型4 | ASTMD638 | 640 | % |
| 断裂,模压成型 | ISO527-2/508 | 640 | % | |
| Tensile elongation at break (MD) | 50.8um | % | ASTM D-882 | 400 |
| 50.8um | % | ISO 527-3 | 400 | |
| Tensile elongation at break (TD) | 50.8um | % | ISO 527-3 | 470 |
| Falling hammer impact | 50.8um | g | ASTM D-1709B | 580 |
| 50.8um | g | ISO 7765-1/B | 580 | |
| Elmendorf Tear Strength (TD) | 50.8um | g | ASTM D-1922 | 510 |
| Elmendorf Tear Strength (MD) | 50.8um | g | ASTM D-1922 | 380 |
| 50.8um | N | ISO 6383-2 | 1700 | |
| Elmendorf Tear Strength (TD) | 50.8um | N | ISO 6383-2 | 2300 |
| Tensile yield strength | Compression Molded | MPa | ASTM D-638 | 8.39 |
| Compression Molded | MPa | ISO 527-2/508 | 8.39 | |
| Tensile fracture strength | Compression Molded | MPa | ASTM D-638 | 22.5 |
| Compression Molded | MPa | ISO 527-2/508 | 22.5 | |
| Tensile strain at break | Compression Molded | % | ASTM D-638 | |
| Compression Molded | % | ISO 527-2/508 | ||
| Film thickness - Tested | um | 50.8 | ||
| Tensile yield strength (MD) | 50.8um | MPa | ASTM D-882 | 11.8 |
| Tensile yield strength (TD) | 50.8um | MPa | ASTM D-882 | 10.9 |
| 50.8um | MPa | ISO 527-3 | 10.9 | |
| Tensile yield strength (MD) | 50.8um | MPa | ISO 527-3 | 11.8 |
| Tensile fracture strength (TD) | 50.8um | MPa | ASTM D-882 | 38.1 |
| Tensile strength at break (MD) | 50.8um | MPa | ASTM D-882 | 37.9 |
| 50.8um | MPa | ISO 527-3 | 37.9 | |
| Tensile fracture strength (TD) | 50.8um | MPa | ISO 527-3 | 38.1 |
| Tensile elongation at break (TD) | 50.8um | % | ASTM D-882 | 470 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | ℃ | ISO 306 | 81.1 | |
| Melting temperature | ℃ | Internal Method | 97.8 | |
| vicat softening point | ℃ | ASTM D-1525 | 81.1 | |
| Vicat softening temperature | ASTMD1525,ISO306 | 81.1 | °C | |
| Melting temperature (DSC) | 内部方法 | 97.8 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | MD:屈服,51µm | ASTMD882 | 11.8 | Mpa |
| TD:屈服,51µm | ASTMD882 | 10.9 | Mpa | |
| MD:屈服,51µm | ISO527-3 | 11.8 | Mpa | |
| TD:屈服,51µm | ISO527-3 | 10.9 | Mpa | |
| MD:断裂,51µm | ASTMD882,ISO527-3 | 37.9 | Mpa | |
| TD:断裂,51µm | ASTMD882,ISO527-3 | 38.1 | Mpa | |
| elongation | MD:断裂,51µm | ASTMD882,ISO527-3 | 400 | % |
| TD:断裂,51µm | ASTMD882,ISO527-3 | 470 | % | |
| Falling hammer impact | 51µm | ASTMD1709B,ISO7765-1/B | 580 | g |
| Elmondov tear strength 5 | MD:51µm | ASTMD1922 | 380 | g |
| TD:51µm | ASTMD1922 | 510 | g | |
| MD:51µm | ISO6383-2 | 1700 | N | |
| TD:51µm | ISO6383-2 | 2300 | N |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| gloss | 45°，50.8um | ASTM D-2457 | ||
| Haze | 50.8um | % | ISO 14782 | |
| 50.8um | % | ASTM D-1003 | ||
| gloss | 45°,50.8µm | ASTMD2457 | 65 | |
| Haze | 50.8µm | ASTMD1003 | 5.8 | % |
| 50.8µm | ISO14782 | 5.8 | % |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 190℃/2.16kg | g/10min | ASTM D-1238 | 1.5 |
| 190℃/2.16kg | g/10min | ISO 1133 | 1.5 | |
| Monomer content | % | Internal Method |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.