Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
EAA 1410 STYRON US
PRIMACOR™
film
High toughness、Heat sealing performance、high strength
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
EAA/STYRON US/1410
Content of comonomer 3
内部方法
%
9
Melt mass flow rate
190°C/2.16kg
ASTMD1238,ISO1133
g/10min
1
Mechanical performance
Test Condition
Test Method
Unit
EAA/STYRON US/1410
Elmendorf Tear Strength (MD)
50.8um
g
380
A
Elmendorf Tear Strength (MD)
50.8um
N
1700
I
Elmendorf Tear Strength (TD)
50.8um
N
2300
I
Elmendorf Tear Strength (TD)
50.8um
g
510
A
Film thickness - Tested
um
50.8
Tensile strength
屈服,模压成型4
ASTMD638
Mpa
8
Tensile strength
屈服,模压成型
ISO527-2/508
Mpa
8
Tensile strength
断裂,模压成型4
ASTMD638
Mpa
2
Tensile strength
断裂,模压成型
ISO527-2/508
Mpa
2
Tensile fracture strength
Compression Molded
MPa
22.5
A
Tensile fracture strength
Compression Molded
MPa
22.5
I
Tensile strength at break (MD)
50.8um
MPa
37.9
A
Tensile strength at break (MD)
50.8um
MPa
37.9
I
Tensile fracture strength (TD)
50.8um
MPa
38.1
I
Tensile fracture strength (TD)
50.8um
MPa
38.1
A
Tensile elongation at break (MD)
50.8um
%
400
A
Tensile elongation at break (MD)
50.8um
%
400
I
Tensile elongation at break (TD)
50.8um
%
470
I
Tensile elongation at break (TD)
50.8um
%
470
A
Tensile yield strength
Compression Molded
MPa
8.39
A
Tensile yield strength
Compression Molded
MPa
8.39
I
Tensile yield strength (MD)
50.8um
MPa
11.8
A
Tensile yield strength (MD)
50.8um
MPa
11.8
I
Tensile yield strength (TD)
50.8um
MPa
10.9
A
Tensile yield strength (TD)
50.8um
MPa
10.9
I
Falling hammer impact
50.8um
g
580
A
Falling hammer impact
50.8um
g
580
I
elongation
断裂,模压成型4
ASTMD638
%
6
elongation
断裂,模压成型
ISO527-2/508
%
6
Thermal performance
Test Condition
Test Method
Unit
EAA/STYRON US/1410
Melting temperature (DSC)
内部方法
°C
9
Melting temperature
℃
97.8
I
vicat softening point
℃
81.1
A
vicat softening point
℃
81.1
I
Vicat softening temperature
ASTMD1525,ISO306
°C
8
film
Test Condition
Test Method
Unit
EAA/STYRON US/1410
Elmondov tear strength 5
MD:51µm
ASTMD1922
g
3
Elmondov tear strength 5
TD:51µm
ASTMD1922
g
5
Elmondov tear strength 5
MD:51µm
ISO6383-2
N
1
Elmondov tear strength 5
TD:51µm
ISO6383-2
N
2
Tensile strength
MD:屈服,51µm
ASTMD882
Mpa
1
Tensile strength
TD:屈服,51µm
ASTMD882
Mpa
1
Tensile strength
MD:屈服,51µm
ISO527-3
Mpa
1
Tensile strength
TD:屈服,51µm
ISO527-3
Mpa
1
Tensile strength
MD:断裂,51µm
ASTMD882,ISO527-3
Mpa
3
Tensile strength
TD:断裂,51µm
ASTMD882,ISO527-3
Mpa
3
Falling hammer impact
51µm
ASTMD1709B,ISO7765-1/B
g
5
elongation
MD:断裂,51µm
ASTMD882,ISO527-3
%
4
elongation
TD:断裂,51µm
ASTMD882,ISO527-3
%
4
optical performance
Test Condition
Test Method
Unit
EAA/STYRON US/1410
Haze
50.8µm
ASTMD1003
%
5
Haze
50.8µm
ISO14782
%
5
Basic performance
Test Condition
Test Method
Unit
EAA/STYRON US/1410
Melt flow rate
190℃/2.16kg
g/10min
1.5
A
Melt flow rate
190℃/2.16kg
g/10min
1.5
I