Physical properties	Test Condition	Test Method	Test Result	Unit
density		ASTM D792/ISO 1183	1.58

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD	ISO294-4	0.70	%
Shrinkage rate	Shrinkage rate	MD	ISO294-4	0.30	%
Water absorption rate	饱和,23°C,2.00mm	ISO62	0.83	%
Water absorption rate	Water absorption rate	平衡,23°C,2.00mm,50%RH	ISO62	0.13	%
MediumDensity			1.32	g/cm³
Top out temperature			170	°C
SpecificHeatCapacity of Melt			1790	J/kg/°C
ThermalConductivityofMelt			0.32	W/m/K
Shrinkage rate, parallel flow direction	3.20 mm	ASTM D955	0.0035	cm/cm
Shrinkage rate, vertical flow direction	3.20 mm	ASTM D955	0.0065	cm/cm
Melt volume flow rate	280°C/5.0kg	ISO1133	5.00	cm3/10min

Mechanical performance	Test Condition	Test Method	Test Result	Unit
TensileCreepModule	1hr	ISO899-1	9350	Mpa
Non notched impact strength		ASTM D256	425	J/m
compressive strength		ASTM D695	141	Mpa
Across Flow		ASTM D638	2.0	%
Low temperature notch impact strength		ASTM D256	43	J/m
Tensile stress	断裂	ISO527-2	85.0	Mpa
Tensile strain	断裂	ISO527-2	2.0	%
Gap impact strength		ASTM D256	64	J/m
Tensile creep modulus	1000hr	ISO899-1	7690	Mpa
Tensile modulus		ASTM D412/ISO 527	10200	kg/cm²(MPa)[Lb/in²]
	Tensile modulus		ISO527-2	10200	Mpa
	Tensile modulus	Tensile modulus		ASTM D638	9930	Mpa
tensile strength		ASTM D638	89.6	Mpa
Rockwell hardness		ASTM D785	75
Bending modulus		ASTM D790/ISO 178	9100	kg/cm²(MPa)[Lb/in²]
	Bending modulus		ASTM D790	9600	Mpa
	Bending modulus	Bending modulus		ISO178	9100	Mpa
bending strength		ASTM D790	141	Mpa
bending strength	bending strength		ASTM D790/ISO 178	141	kg/cm²(MPa)[Lb/in²]
Tensile elongation at break (elongation at break)		ASTM D638/ISO 527	2.0	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
Flame retardant grade		UL 94	HB
Linear coefficient of thermal expansion	MD：--	ISO11359-2	1.6E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to23°C	ISO11359-2	2.6E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：--	ISO11359-2	5.2E-05	cm/cm/°C
			Linear coefficient of thermal expansion	TD：-40to23°C	ISO11359-2	5.3E-05	cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：EffectiveThermalDiffusivity	ISO11359-2	1.4E-07	m²/s
Hot deformation temperature		ASTM D648/ISO 75	235	℃（℉）
	Hot deformation temperature	66 psi，未退火	ASTM D648	241	°C
		Hot deformation temperature	264 psi，未退火	ASTM D648	215	°C
			Hot deformation temperature	0.45MPa,未退火	ISO75-2/B	235	°C
			Hot deformation temperature	Hot deformation temperature	1.8MPa,未退火	ISO75-2/A	200	°C
melting point			252	°C
Linear coefficient of thermal expansion, parallel flow direction		ASTM E831	0.000016	cm/cm/ ℃
Vicat softening temperature		ISO306/B50	205	°C
Melting temperature 2		ISO11357-3	252	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation factor	100Hz	IEC60250	0.030
Dissipation factor	Dissipation factor	1MHz	IEC60250	0.014
Relative permittivity	100Hz	IEC60250	4.50
Relative permittivity	Relative permittivity	1MHz	IEC60250	4.10
Leakage Trace Index		IEC60112	300	V
Dielectric strength		IEC60243-1	39	KV/mm
Surface resistivity		IEC60093	1E+14	ohms
Volume resistivity		IEC60093	1E+15	ohms·cm

Processing performance	Test Condition	Test Method	Test Result	Unit
Melt Temperature			280-300	%

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	20	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	25	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M计秤	ISO2039-2	75
Rockwell hardness	Rockwell hardness	R计秤	ISO2039-2	115

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.75mm	UL94	HB
	UL flame retardant rating	1.5mm	UL94	HB
		UL flame retardant rating	0.75mm	IEC60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC60695-11-10,-20	HB
Extreme Oxygen Index		ISO4589-2	21	%
FMVSS flammability		FMVSS302	B
Fogging-G-value	condensate	ISO6452	1E-04	g
Burning rate 3	1.00mm	ISO3795	<100	mm/min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.