PET Rynite® 935 NC010 DUPONT USA
141
- Unit Price:
- $2901 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 29.1MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced High temperature resistan
- Application Areas:household electrical appl Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.58 |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 0.70 | % |
| MD | ISO294-4 | 0.30 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 0.83 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.13 | % | |
| MediumDensity | 1.32 | g/cm³ | ||
| Top out temperature | 170 | °C | ||
| SpecificHeatCapacity of Melt | 1790 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.32 | W/m/K | ||
| Shrinkage rate, parallel flow direction | 3.20 mm | ASTM D955 | 0.0035 | cm/cm |
| Shrinkage rate, vertical flow direction | 3.20 mm | ASTM D955 | 0.0065 | cm/cm |
| Melt volume flow rate | 280°C/5.0kg | ISO1133 | 5.00 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| TensileCreepModule | 1hr | ISO899-1 | 9350 | Mpa |
| Non notched impact strength | ASTM D256 | 425 | J/m | |
| compressive strength | ASTM D695 | 141 | Mpa | |
| Across Flow | ASTM D638 | 2.0 | % | |
| Low temperature notch impact strength | ASTM D256 | 43 | J/m | |
| Tensile stress | Break | ISO527-2 | 85.0 | Mpa |
| Tensile strain | Break | ISO527-2 | 2.0 | % |
| Gap impact strength | ASTM D256 | 64 | J/m | |
| Tensile creep modulus | 1000hr | ISO899-1 | 7690 | Mpa |
| Tensile modulus | ASTM D412/ISO 527 | 10200 | kg/cm²(MPa)[Lb/in²] | |
| ISO527-2 | 10200 | Mpa | ||
| ASTM D638 | 9930 | Mpa | ||
| tensile strength | ASTM D638 | 89.6 | Mpa | |
| Rockwell hardness | ASTM D785 | 75 | ||
| Bending modulus | ASTM D790/ISO 178 | 9100 | kg/cm²(MPa)[Lb/in²] | |
| ASTM D790 | 9600 | Mpa | ||
| ISO178 | 9100 | Mpa | ||
| bending strength | ASTM D790 | 141 | Mpa | |
| ASTM D790/ISO 178 | 141 | kg/cm²(MPa)[Lb/in²] | ||
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 2.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame retardant grade | UL 94 | HB | ||
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 1.6E-05 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 2.6E-05 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 5.2E-05 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 5.3E-05 | cm/cm/°C | |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 1.4E-07 | m²/s | |
| Hot deformation temperature | ASTM D648/ISO 75 | 235 | ℃（℉） | |
| 66 psi， Unannealed | ASTM D648 | 241 | °C | |
| 264 psi，Unannealed | ASTM D648 | 215 | °C | |
| 0.45MPa,Unannealed | ISO75-2/B | 235 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 200 | °C | |
| melting point | 252 | °C | ||
| Linear coefficient of thermal expansion, parallel flow direction | ASTM E831 | 0.000016 | cm/cm/ ℃ | |
| Vicat softening temperature | ISO306/B50 | 205 | °C | |
| Melting temperature 2 | ISO11357-3 | 252 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation factor | 100Hz | IEC60250 | 0.030 | |
| 1MHz | IEC60250 | 0.014 | ||
| Relative permittivity | 100Hz | IEC60250 | 4.50 | |
| 1MHz | IEC60250 | 4.10 | ||
| Leakage Trace Index | IEC60112 | 300 | V | |
| Dielectric strength | IEC60243-1 | 39 | KV/mm | |
| Surface resistivity | IEC60093 | 1E+14 | ohms | |
| Volume resistivity | IEC60093 | 1E+15 | ohms·cm |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Temperature | 280-300 | % |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 20 | kJ/m² |
| 23°C | ISO179/1eU | 25 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Sale | ISO2039-2 | 75 | |
| R-Sale | ISO2039-2 | 115 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.75mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 21 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| Fogging-G-value | condensate | ISO6452 | 1E-04 | g |
| Burning rate 3 | 1.00mm | ISO3795 | <100 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.