Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.01 | kg·cm/cm(J/M)ft·lb/in |
| Water absorption rate 23 ℃/24h | | ASTM D570/ISO 62 | 1.5 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | TD | ISO294-4 | 1.2 | % |
| Shrinkage rate | MD | ISO294-4 | 0.85 | % |
| Water absorption rate | 饱和,23°C | ISO62 | 1.5 | % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.80 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | 屈服 | ISO527-2 | 45.0 | Mpa |
| Tensile strain | 屈服 | ISO527-2 | 5.0 | % |
| Tensile strain | 断裂 | ISO527-2 | >50 | % |
| elongation at break | | ASTM D412/ISO 527 | >50 | % |
| Tensile modulus | | ASTM D412/ISO 527 | 1350 | kg/cm²(MPa)[Lb/in²] |
| Tensile modulus | | ISO527-2 | 1350 | Mpa |
| elongation | | ASTM D412/ISO 527 | 5 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | | ASTM D648/ISO 75 | 50 | ℃（℉） |
| Hot deformation temperature | | ASTM D648/ISO 75 | 110 | ℃（℉） |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 50.0 | °C |
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 110 | °C |
| melting point | | | 178 | ℃（℉） |
| Vicat softening temperature | -- | ISO306/A | 170 | °C |
| Vicat softening temperature | -- | ISO306/B | 140 | °C |
| Melting temperature 2 | | ISO11357-3 | 178 | °C |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO11359-2 | 1.5E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric strength | | IEC60243-1 | 27 | KV/mm |
| Relative permittivity | 23°C,100Hz | IEC60250 | 3.80 | |
| Relative permittivity | 23°C,1MHz | IEC60250 | 2.50 | |
| Leakage Trace Index | -- | IEC60112 | 600 | V |
| Leakage Trace Index | SolutionA3 | IEC60112 | >600 | V |
| Dissipation factor | 23°C,1MHz | IEC60250 | 0.031 | |
| Dissipation factor | 23°C,100Hz | IEC60250 | 0.045 | |
| Volume resistivity | | IEC60093 | 1E+15 | ohms·cm |
| Volume resistivity | | ASTM D257/IEC 60093 | 10^15 | Ω.cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | NoBreak | |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | NoBreak | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.6mm | UL94 | HB | |
| UL flame retardant rating | 3.2mm | UL94 | HB | |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| ElectrolyticalCorrosion | | IEC60426 | A1 | |
| ISO Shortcut | | ISO1874 | PA12,KH,18-010 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.