PA12 VESTAMID® L1940 EVONIK GERMANY

247

Unit Price:
$18256 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:low density High elasticity Photostability Low temperature impact re Oil resistant Low friction coefficient Thermal stability Resistance to stress crac wear resistant
Application Areas:Cable sheath Pipe fittings Optic fibre cable
Color:--
Grade:Injection grade

Technical Data Sheet Compare

Physical properties	Test Condition	Test Method	Test Result	Unit
density		ASTM D792/ISO 1183	1.01	kg·cm/cm(J/M)ft·lb/in
Water absorption rate 23 ℃/24h		ASTM D570/ISO 62	1.5	%

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD	ISO294-4	1.2	%
Shrinkage rate	Shrinkage rate	MD	ISO294-4	0.85	%
Water absorption rate	Saturation,23°C	ISO62	1.5	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO62	0.80	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile stress	Yield	ISO527-2	45.0	Mpa
Tensile strain	Yield	ISO527-2	5.0	%
Tensile strain	Tensile strain	Break	ISO527-2	>50	%
elongation at break		ASTM D412/ISO 527	>50	%
Tensile modulus		ASTM D412/ISO 527	1350	kg/cm²(MPa)[Lb/in²]
Tensile modulus	Tensile modulus		ISO527-2	1350	Mpa
elongation		ASTM D412/ISO 527	5	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature		ASTM D648/ISO 75	50	℃（℉）
	Hot deformation temperature		ASTM D648/ISO 75	110	℃（℉）
		Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	50.0	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	110	°C
melting point			178	℃（℉）
Vicat softening temperature	--	ISO306/A	170	°C
Vicat softening temperature	Vicat softening temperature	--	ISO306/B	140	°C
Melting temperature 2		ISO11357-3	178	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO11359-2	1.5E-04	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength		IEC60243-1	27	KV/mm
Relative permittivity	23°C,100Hz	IEC60250	3.80
Relative permittivity	Relative permittivity	23°C,1MHz	IEC60250	2.50
Leakage Trace Index	--	IEC60112	600	V
Leakage Trace Index	Leakage Trace Index	SolutionA3	IEC60112	>600	V
Dissipation factor	23°C,1MHz	IEC60250	0.031
Dissipation factor	Dissipation factor	23°C,100Hz	IEC60250	0.045
Volume resistivity		IEC60093	1E+15	ohms·cm
Volume resistivity	Volume resistivity		ASTM D257/IEC 60093	10^15	Ω.cm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	NoBreak

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.6mm	UL94	HB
UL flame retardant rating	UL flame retardant rating	3.2mm	UL94	HB

Supplementary Information	Test Condition	Test Method	Test Result	Unit
ElectrolyticalCorrosion		IEC60426	A1
ISO Shortcut		ISO1874	PA12,KH,18-010

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.