Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 6.3 | % |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO62 | 1.9 | % |
| Shrinkage rate | TD | ISO294-4 | 0.60 | % |
| Shrinkage rate | MD | ISO294-4 | 0.20 | % |
| MediumDensity | | | 1.20 | g/cm³ |
| SpecificHeatCapacity of Melt | | | 2280 | J/kg/°C |
| ThermalConductivityofMelt | | | 0.26 | W/m/K |
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 15.0 | cm3/10min |
| Density/specific gravity | | ISO1183 | 1.36 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending modulus 2 | | ISO178 | 8500 | Mpa |
| Bending stress 2 | | ISO178 | 280 | Mpa |
| TensileCreepModule | 1hr | ISO899-1 | -- | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | -- | Mpa |
| Tensile stress | 断裂 | ISO527-2 | 190 | Mpa |
| Tensile strain | 断裂 | ISO527-2 | 3.5 | % |
| Tensile modulus | | ISO527-2 | 9500 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 220 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 210 | °C |
| Vicat softening temperature | | ISO306/B50 | 215 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 2.6E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO11359-2 | 7.5E-05 | cm/cm/°C |
| EffectiveThermalDiffusivity | | | 9.1E-08 | m²/s |
| Melting temperature 5 | | ISO11357-3 | 221 | °C |
| Glass transition temperature 3 | | ISO11357-2 | 60.0 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Multi axis Instrumented Impact Energy | 23°C | ISO6603-2 | 3.50 | J |
| Unscented Izod impact strength | 23°C | ISO180/1U | 80 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 10 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 16 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 10 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 15 | kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 80 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 100 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R级 | ISO2039-2 | 121 | |
| Ball pressure hardness | H961/30 | ISO2039-1 | 230 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| UL flame retardant rating | 0.75mm | IEC60695-11-10,-20 | HB | |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
| FMVSS flammability | | FMVSS302 | B | |
| Burning rate 4 | 1.00mm | ISO3795 | 50 | mm/min |
| Extreme Oxygen Index 5 | | ISO4589-2 | 21 | % |
| atomization | F-value(refraction) | ISO6452 | 95 | % |
| atomization | G-value(condensate) | ISO6452 | 1E-04 | g |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| EmissionofOrganicCompounds | | VDA277 | 8.50 | µgC/g |
| Odor | | VDA270 | 3.50 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.