PA66 Zytel® 73G30HSL DUPONT USA
131
Unit Price:$3105 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 100.9MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability 30% filler by weight Filler: Glass fiber reinf
- Application Areas:Electronic and electrical Automotive Applications
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 吸水率 | 饱和,23°C,2.00mm | ISO62 | 6.3 | % |
| 平衡,23°C,2.00mm,50%RH | ISO62 | 1.9 | % | |
| 收缩率 | TD | ISO294-4 | 0.60 | % |
| MD | ISO294-4 | 0.20 | % | |
| MeltDensity | 1.20 | g/cm³ | ||
| SpecificHeatCapacityofMelt | 2280 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.26 | W/m/K | ||
| 熔体体积流动速率 | 250°C/5.0kg | ISO1133 | 15.0 | cm3/10min |
| 密度 / 比重 | ISO1183 | 1.36 | g/cm³ |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 弯曲模量2 | ISO178 | 8500 | Mpa | |
| 弯曲应力2 | ISO178 | 280 | Mpa | |
| TensileCreepModulus | 1hr | ISO899-1 | -- | Mpa |
| 拉伸蠕变模量 | 1000hr | ISO899-1 | -- | Mpa |
| 拉伸应力 | 断裂 | ISO527-2 | 190 | Mpa |
| 拉伸应变 | 断裂 | ISO527-2 | 3.5 | % |
| 拉伸模量 | ISO527-2 | 9500 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 热变形温度 | 0.45MPa,未退火 | ISO75-2/B | 220 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 210 | °C | |
| 维卡软化温度 | ISO306/B50 | 215 | °C | |
| 线形热膨胀系数 | MD | ISO11359-2 | 2.6E-05 | cm/cm/°C |
| TD | ISO11359-2 | 7.5E-05 | cm/cm/°C | |
| EffectiveThermalDiffusivity | 9.1E-08 | m²/s | ||
| 熔融温度5 | ISO11357-3 | 221 | °C | |
| 玻璃转化温度3 | ISO11357-2 | 60.0 | °C |
| 冲击性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 多轴向仪器化冲击能量 | 23°C | ISO6603-2 | 3.50 | J |
| 无缺口伊佐德冲击强度 | 23°C | ISO180/1U | 80 | kJ/m² |
| 简支梁缺口冲击强度 | -30°C | ISO179/1eA | 10 | kJ/m² |
| 23°C | ISO179/1eA | 16 | kJ/m² | |
| 悬壁梁缺口冲击强度 | -30°C | ISO180/1A | 10 | kJ/m² |
| 23°C | ISO180/1A | 15 | kJ/m² | |
| 简支梁无缺口冲击强度 | -30°C | ISO179/1eU | 80 | kJ/m² |
| 23°C | ISO179/1eU | 100 | kJ/m² |
| 硬度 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 洛氏硬度 | R级 | ISO2039-2 | 121 | |
| 球压硬度 | H961/30 | ISO2039-1 | 230 | Mpa |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL阻燃等级 | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.75mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| FMVSS可燃性 | FMVSS302 | B | ||
| 燃烧速率4 | 1.00mm | ISO3795 | 50 | mm/min |
| 极限氧指数5 | ISO4589-2 | 21 | % | |
| 雾化 | F-value(refraction) | ISO6452 | 95 | % |
| G-value(condensate) | ISO6452 | 1E-04 | g |
| 补充信息 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 8.50 | µgC/g | |
| Odor | VDA270 | 3.50 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.