Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt volume flow rate | 265°C/5.0kg | ISO1133 | 22.0 | cm3/10min |
| Shrinkage rate | TD2 | ISO2577 | 0.60to0.80 | % |
| Shrinkage rate | TD:90°C,1hr | ISO2577 | 0.10to0.20 | % |
| Shrinkage rate | MD2 | ISO2577 | 0.60to0.80 | % |
| Shrinkage rate | MD:90°C,1hr | ISO2577 | 0.10to0.20 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | 23°C | ISO527-2/1 | 2250 | Mpa |
| Tensile stress | 屈服,23°C | ISO527-2/50 | 55.0 | Mpa |
| Tensile stress | 断裂,23°C | ISO527-2/50 | 50.0 | Mpa |
| Tensile strain | 屈服,23°C | ISO527-2/50 | 5.0 | % |
| Nominal tensile fracture strain | 23°C | ISO527-2/50 | >50 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 125 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 110 | °C |
| Vicat softening temperature | | ISO306/B120 | 140 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | -30°C | ISO180/1C | NoBreak | |
| Impact strength of cantilever beam gap | -20°C | ISO180/A | 40 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/A | 50 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1C | NoBreak | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.