Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.27 | |
| Molding shrinkage rate | | ASTM D955 | 0.2 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | | ASTM D-955 | 0.30-0.60 | % |
| Water absorption rate | | ASTM D-570 | 0.2 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.20 | % |
| Colorb-Hunter3 | | ASTME308 | <1.00 | |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Gap impact strength | | ASTM D-256 | 100 | J/m |
| Tensile strength | 屈服 | ASTMD638 | 53.0 | Mpa |
| Tensile strength | 断裂 | ASTMD638 | 26.0 | Mpa |
| Tensile strength (yield) | | ASTM D-638 | 50 | Mpa |
| Tensile strength (fracture) | | ASTM D-638 | 28 | Mpa |
| Elongation rate 4 | 屈服 | ASTMD638 | 5.0 | % |
| Elongation rate 4 | 断裂 | ASTMD638 | 70 | % |
| Bending strength 5 | | ASTMD790 | 80.0 | Mpa |
| elongation at break | | ASTM D412/ISO 527 | 70 | % |
| elongation | | ASTM D-638 | 140 | % |
| Rockwell hardness | | ASTM D785 | 116 | kg·cm/cm(J/M)ft·lb/in |
| Bending modulus | | ASTM D790/ISO 178 | 2150 | kg/cm²(MPa)[Lb/in²] |
| Bending modulus | | ASTM D-790 | 2100 | Mpa |
| Bending modulus | | ASTMD790 | 2150 | Mpa |
| bending strength | | ASTM D-790 | 73 | Mpa |
| bending strength | | ASTM D790/ISO 178 | 80 | kg/cm²(MPa)[Lb/in²] |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | | ASTM D-648 | 70 | °C |
| Hot deformation temperature | 0.45MPa,未退火 | ASTMD648 | 74.0 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ASTMD648 | 70.0 | °C |
| Vicat softening temperature | | ASTMD15256 | 83.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation factor | 1kHz | ASTMD150 | 5E-03 | |
| Dissipation factor | 1MHz | ASTMD150 | 0.023 | |
| Dielectric strength 7 | | ASTMD149 | 16 | KV/mm |
| Surface resistivity | | ASTMD257 | 1E+16 | ohms |
| Dielectric constant | 1MHz | ASTMD150 | 2.40 | |
| Dielectric constant | 1kHz | ASTMD150 | 2.60 | |
| Volume resistivity | | ASTMD257 | 1E+15 | ohms·cm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R级 | ASTMD785 | 116 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Light transmittance | | ASTM D1003/ISO 13468 | 89.0 | % |
| Refractive index | | ASTM D542/ISO 489 | 1.570 | |
| Refractive index | | ASTMD542 | 1.570 | |
| gloss | 60° | ASTME308 | 159 | |
| Haze | | ASTMD1003 | <1.0 | % |
| transmissivity | | ASTMD1003 | 89.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.0mm | UL94 | HB | |
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| UL flame retardant rating | 3.0mm | UL94 | V-2 | |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D-792 | 1.27 | g/cm³ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.