PETG SKYGREEN® K2012 SK KOREA

362

Unit Price:
$2441 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
377MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Easy to process Antichemical High toughness High gloss
Application Areas:packing film sheet bottle container Toy
Color:--
Grade:Extrusion grade

Technical Data Sheet Compare

Physical properties	Test Condition	Test Method	Test Result	Unit
density		ASTM D792/ISO 1183	1.27
Molding shrinkage rate		ASTM D955	0.2	%

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate		ASTM D-955	0.30-0.60	%
Water absorption rate		ASTM D-570	0.2	%
Water absorption rate	Water absorption rate	24hr	ASTMD570	0.20	%
Colorb-Hunter3		ASTME308	<1.00

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile strength	Yield	ASTMD638	53.0	Mpa
Tensile strength	Tensile strength	Break	ASTMD638	26.0	Mpa
Elongation rate 4	Yield	ASTMD638	5.0	%
Elongation rate 4	Elongation rate 4	Break	ASTMD638	70	%
Tensile strength (yield)		ASTM D-638	50	Mpa
Tensile strength (fracture)		ASTM D-638	28	Mpa
Bending modulus		ASTM D-790	2100	Mpa
bending strength		ASTM D-790	73	Mpa
elongation		ASTM D-638	140	%
Gap impact strength		ASTM D-256	100	J/m
Bending modulus		ASTM D790/ISO 178	2150	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	80	kg/cm²(MPa)[Lb/in²]
elongation at break		ASTM D412/ISO 527	70	%
Rockwell hardness		ASTM D785	116	kg·cm/cm(J/M)ft·lb/in
Bending modulus		ASTMD790	2150	Mpa
Bending strength 5		ASTMD790	80.0	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ASTMD648	74.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	70.0	°C
Vicat softening temperature		ASTMD15256	83.0	°C
Hot deformation temperature		ASTM D-648	70	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		ASTMD257	1E+16	ohms
Volume resistivity		ASTMD257	1E+15	ohms·cm
Dielectric strength 7		ASTMD149	16	KV/mm
Dielectric constant	1kHz	ASTMD150	2.60
Dielectric constant	Dielectric constant	1MHz	ASTMD150	2.40
Dissipation factor	1kHz	ASTMD150	5E-03
Dissipation factor	Dissipation factor	1MHz	ASTMD150	0.023

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ASTMD785	116

optical performance	Test Condition	Test Method	Test Result	Unit
gloss	60°	ASTME308	159
Refractive index		ASTMD542	1.570
transmissivity		ASTMD1003	89.0	%
Haze		ASTMD1003	<1.0	%
Light transmittance		ASTM D1003/ISO 13468	89.0	%
Refractive index		ASTM D542/ISO 489	1.570

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.0mm	UL94	HB
	UL flame retardant rating	1.5mm	UL94	HB
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	V-2

Basic performance	Test Condition	Test Method	Test Result	Unit
density		ASTM D-792	1.27	g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.