PA6/66 Ultramid® C3U BASF GERMANY

392

Properties:
High impact resistance
Flame retardant
Usages:
Electrical components
Electronic insulation
Certificates:
UL
Compare
View Prices

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD：3.18mm		0.80	%
Water absorption rate	饱和	ASTMD570	8.5	%
	Water absorption rate	饱和,23°C	ISO62	8.5	%
		Water absorption rate	平衡,50%RH	ASTMD570	2.9	%
		Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO62	2.9	%
Melt volume flow rate	275°C/5.0kg	ISO1133	140	cm3/10min
Density/specific gravity		ASTMD792	1.16	g/cm³
Density/specific gravity	Density/specific gravity		ISO1183	1.16	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile strength	屈服,23°C	ASTMD638	83.0	Mpa
Nominal tensile fracture strain	23°C	ISO527-2	6.0	%
Tensile stress	屈服,23°C	ISO527-2	75.0	Mpa
Tensile strain	屈服,23°C	ISO527-2	4.0	%
Tensile modulus	23°C	ISO527-2	3500	Mpa
elongation	断裂,23°C	ASTMD638	50	%
elongation	elongation	屈服,23°C	ASTMD638	5.0	%
Bending modulus	23°C	ASTMD790	3000	Mpa
Bending modulus	Bending modulus	23°C	ISO178	3000	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,未退火	ASTMD648	224	°C
	Hot deformation temperature	1.8MPa,未退火	ASTMD648	91.0	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,未退火	ISO75-2/A	70.0	°C
RTIElec	0.38mm	UL746	110	°C
	RTIElec	0.75mm	UL746	120	°C
		RTIElec	1.5mm	UL746	120	°C
		RTIElec	RTIElec	3.0mm	UL746	120	°C
Evolution Calendar intelligent importer	0.38mm	UL746	65.0	°C
	Evolution Calendar intelligent importer	0.75mm	UL746	105	°C
		Evolution Calendar intelligent importer	1.5mm	UL746	105	°C
		Evolution Calendar intelligent importer	Evolution Calendar intelligent importer	3.0mm	UL746	105	°C
RTIStr	0.38mm	UL746	65.0	°C
	RTIStr	0.75mm	UL746	115	°C
		RTIStr	1.5mm	UL746	120	°C
		RTIStr	RTIStr	3.0mm	UL746	120	°C
Peak melting temperature		ASTMD3418	243	°C
Melting temperature (DSC)		ISO3146	243	°C
Linear coefficient of thermal expansion	MD	ASTME831	4E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD		8E-05	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD		9E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength		IEC60243-1	32	KV/mm
Leakage Trace Index		IEC60112	600	V
VolumeResistivity	1.50mm	ASTMD257	1E+13	ohms·cm
Dissipation factor	1MHz	IEC60250	0.020
Dielectric constant	1MHz	IEC60250	3.60
Volume resistivity		IEC60093	1E+13	ohms·cm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C	ISO179	80	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO179	4.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179	9.0	kJ/m²
Impact strength of cantilever beam gap	-40°C	ASTMD256	32	J/m
	Impact strength of cantilever beam gap	23°C	ASTMD256	43	J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO180	4.5	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness		ISO2039-1	100	Mpa

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.38mm	UL94	V-0
	UL flame retardant rating	0.75mm	UL94	V-0
		UL flame retardant rating	1.5mm	UL94	V-0
		UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

PA6/66 Ultramid® C3U BASF GERMANY

Technical Data Sheet