PEI ULTEM™ 1000 WH SABIC INNOVATIVE US

338

Properties:
Glass fiber reinforced
Flame retardant
enhance
Usages:
Electrical field
Electronic field
Automotive sector
Certificates:
UL
Compare
View Prices

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Molten Volume Flow Rate (MVR)	360°C/5.0 kg	ISO 1133	13.0	cm3/10min
Shrinkage rate - Flow 1		内部方法	0.50 到 0.70	%
Water absorption rate	饱和, 23°C	ISO 62	1.3	%
Water absorption rate	Water absorption rate	平衡, 23°C, 50% RH	ISO 62	0.70	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ISO 527-2/1	3200	Mpa
Tensile stress	屈服	ISO 527-2/50	105	Mpa
Tensile stress	Tensile stress	断裂	ISO 527-2/50	85.0	Mpa
Tensile strain	屈服	ISO 527-2/50	6.0	%
Tensile strain	Tensile strain	断裂	ISO 527-2/50	60	%
Bending modulus 2		ISO 178	3300	Mpa
Bending stress 2, 3		ISO 178	160	Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 转轮	内部方法	10.0	mg

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature 6	0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距	ISO 75-2/Be	200	°C
Hot deformation temperature 6	Hot deformation temperature 6	1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距	ISO 75-2/Ae	190	°C
Vicat softening temperature	--	ISO 306/A50	215	°C
	Vicat softening temperature	--	ISO 306/B50	211	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	212	°C
Ball Pressure Test	123 到 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	流动 : 23 到 150°C	ISO 11359-2	5.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向 : 23 到 150°C	ISO 11359-2	5.0E-5	cm/cm/°C
thermal conductivity		ISO 8302	0.24	W/m/K
RTI Elec		UL 746	170	°C
RTI Imp		UL 746	170	°C
RTI		UL 746	170	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC 60093	> 1.0E+15	ohms
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Dielectric strength	0.800 mm, 在油中	IEC 60243-1	33	KV/mm
	Dielectric strength	1.60 mm, 在油中	IEC 60243-1	25	KV/mm
	Dielectric strength	Dielectric strength	3.20 mm, 在油中	IEC 60243-1	16	KV/mm
Relative permittivity	50 Hz	IEC 60250	2.90
	Relative permittivity	60 Hz	IEC 60250	2.90
	Relative permittivity	Relative permittivity	1 MHz	IEC 60250	2.90
Dissipation factor	50 Hz	IEC 60250	5.0E-4
	Dissipation factor	60 Hz	IEC 60250	5.0E-4
		Dissipation factor	1 MHz	IEC 60250	6.0E-3
		Dissipation factor	Dissipation factor	2.45 GHz	IEC 60250	2.5E-3
Leakage Trace Index	--	IEC 60112	150	V
Leakage Trace Index	Leakage Trace Index	解决方案 B	IEC 60112	100	V

injection	Test Result	Unit
drying temperature	150	°C
drying time	4.0 到 6.0	hr
Suggested maximum moisture content	0.020	%
Hopper temperature	80 到 120	°C
Temperature at the rear of the barrel	340 到 395	°C
Temperature in the middle of the barrel	350 到 405	°C
Temperature at the front of the material cylinder	360 到 415	°C
Spray nozzle temperature	350 到 405	°C
Processing (melt) temperature	370 到 410	°C
Mold temperature	140 到 180	°C

Impact performance	Test Condition	Test Method	Test Result	Unit
Suspended wall beam gap impact strength 5	-30°C	ISO 180/1A	6.0	kJ/m²
Suspended wall beam gap impact strength 5	Suspended wall beam gap impact strength 5	23°C	ISO 180/1A	6.0	kJ/m²
Unscented Izod Impact Strength 5	-30°C	ISO 180/1U	无断裂
Unscented Izod Impact Strength 5	Unscented Izod Impact Strength 5	23°C	ISO 180/1U	无断裂

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness	H 358/30	ISO 2039-1	140	Mpa

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.40 mm	UL 94	V-2
	UL flame retardant rating	0.75 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA
Burning wire flammability index	3.2 mm	IEC 60695-2-12	960	°C
Extreme Oxygen Index		ISO 4589-2	47	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

PEI ULTEM™ 1000 WH SABIC INNOVATIVE US

Technical Data Sheet