PEI ULTEM™ 1000 WH SABIC INNOVATIVE US
242
Unit Price:$21527 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Flame retardant enhance
- Application Areas:Electrical field Electronic field Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 吸水率 | 饱和, 23°C | ISO 62 | 1.3 | % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.70 | % | |
| 熔融体积流量（MVR） | 360°C/5.0 kg | ISO 1133 | 13.0 | cm3/10min |
| 收缩率 - 流动 1 | 内部方法 | 0.50 到 0.70 | % |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 弯曲应力 2, 3 | ISO 178 | 160 | Mpa | |
| 泰伯耐磨性 | 1000 Cycles, 1000 g, CS-17 转轮 | 内部方法 | 10.0 | mg |
| 弯曲模量 2 | ISO 178 | 3300 | Mpa | |
| 拉伸应力 | 屈服 | ISO 527-2/50 | 105 | Mpa |
| 断裂 | ISO 527-2/50 | 85.0 | Mpa | |
| 拉伸应变 | 屈服 | ISO 527-2/50 | 6.0 | % |
| 断裂 | ISO 527-2/50 | 60 | % | |
| 拉伸模量 | ISO 527-2/1 | 3200 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 维卡软化温度 | -- | ISO 306/A50 | 215 | °C |
| -- | ISO 306/B50 | 211 | °C | |
| -- | ISO 306/B120 | 212 | °C | |
| 线形热膨胀系数 | 流动 : 23 到 150°C | ISO 11359-2 | 5.0E-5 | cm/cm/°C |
| 横向 : 23 到 150°C | ISO 11359-2 | 5.0E-5 | cm/cm/°C | |
| Ball Pressure Test | 123 到 127°C | IEC 60695-10-2 | 通过 | |
| 导热系数 | ISO 8302 | 0.24 | W/m/K | |
| RTI | UL 746 | 170 | °C | |
| RTI Imp | UL 746 | 170 | °C | |
| RTI Elec | UL 746 | 170 | °C | |
| 热变形温度 6 | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Be | 200 | °C |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Ae | 190 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 相对电容率 | 50 Hz | IEC 60250 | 2.90 | |
| 60 Hz | IEC 60250 | 2.90 | ||
| 1 MHz | IEC 60250 | 2.90 | ||
| 漏电起痕指数 | -- | IEC 60112 | 150 | V |
| 解决方案 B | IEC 60112 | 100 | V | |
| 介电强度 | 0.800 mm, 在油中 | IEC 60243-1 | 33 | KV/mm |
| 1.60 mm, 在油中 | IEC 60243-1 | 25 | KV/mm | |
| 3.20 mm, 在油中 | IEC 60243-1 | 16 | KV/mm | |
| 表面电阻率 | IEC 60093 | > 1.0E+15 | ohms | |
| 体积电阻率 | IEC 60093 | 1.0E+15 | ohms·cm | |
| 耗散因数 | 50 Hz | IEC 60250 | 5.0E-4 | |
| 60 Hz | IEC 60250 | 5.0E-4 | ||
| 1 MHz | IEC 60250 | 6.0E-3 | ||
| 2.45 GHz | IEC 60250 | 2.5E-3 |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥温度 | 150 | °C | ||
| 建议的最大水分含量 | 0.020 | % | ||
| 加工（熔体）温度 | 370 到 410 | °C | ||
| 模具温度 | 140 到 180 | °C | ||
| 干燥时间 | 4.0 到 6.0 | hr | ||
| 料筒后部温度 | 340 到 395 | °C | ||
| 料筒中部温度 | 350 到 405 | °C | ||
| 料筒前部温度 | 360 到 415 | °C | ||
| 射嘴温度 | 350 到 405 | °C | ||
| 料斗温度 | 80 到 120 | °C |
| 冲击性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 悬壁梁缺口冲击强度 5 | -30°C | ISO 180/1A | 6.0 | kJ/m² |
| 23°C | ISO 180/1A | 6.0 | kJ/m² | |
| 无缺口伊佐德冲击强度 5 | -30°C | ISO 180/1U | 无断裂 | |
| 23°C | ISO 180/1U | 无断裂 |
| 硬度 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 球压硬度 | H 358/30 | ISO 2039-1 | 140 | Mpa |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 灼热丝易燃指数 | 3.2 mm | IEC 60695-2-12 | 960 | °C |
| 极限氧指数 | ISO 4589-2 | 47 | % | |
| UL 阻燃等级 | 0.40 mm | UL 94 | V-2 | |
| 0.75 mm | UL 94 | V-0 | ||
| 3.0 mm | UL 94 | 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.