ASA/PC GELOY™ CR7500-GY SABIC INNOVATIVE US
657
- Properties:Thermal stabilityAntistaticHigh mobility
- Usages:Electrical applicationsAutomotive Applications
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 220°C/10.0 kg | ASTM D1238 | 6.3 | g/10 min |
| 260°C/5.0 kg | ASTM D1238 | 11 | g/10 min | |
| Molten Volume Flow Rate (MVR) | 220°C/10.0 kg | ISO 1133 | 6.00 | cm3/10min |
| 260°C/5.0 kg | ISO 1133 | 10.0 | cm3/10min | |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.80 | % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.50 | % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.20 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | -- 2 | ASTM D638 | 1970 | Mpa |
| -- | ISO 527-2/1 | 2040 | Mpa | |
| Tensile strength | 屈服 3 | ASTM D638 | 40.0 | Mpa |
| 屈服 | ISO 527-2/5 | 43.0 | Mpa | |
| 断裂 3 | ASTM D638 | 33.0 | Mpa | |
| 断裂 | ISO 527-2/5 | 35.0 | Mpa | |
| elongation | 屈服 3 | ASTM D638 | 3.6 | % |
| 屈服 | ISO 527-2/5 | 3.3 | % | |
| 断裂 3 | ASTM D638 | 60 | % | |
| 断裂 | ISO 527-2/5 | 19 | % | |
| Bending modulus | 50.0 mm 跨距 4 | ASTM D790 | 2170 | Mpa |
| -- 5 | ISO 178 | 2060 | Mpa | |
| Bending stress | -- 5, 6 | ISO 178 | 64.0 | Mpa |
| 屈服, 50.0 mm 跨距 4 | ASTM D790 | 68.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 90.0 | °C |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 9 | ISO 75-2/Ae | 88.0 | °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8 | ISO 75-2/Af | 89.0 | °C | |
| Vicat softening temperature | -- | ASTM D152510 | 98.0 | °C |
| -- | ISO 306/B50 | 102 | °C | |
| -- | ISO 306/B120 | 105 | °C | |
| Ball Pressure Test | 98°C | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831, ISO 11359-2 | 8.4E-5 | cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 9.5E-5 | cm/cm/°C | |
| 横向 : -40°C | ISO 11359-2 | 9.5E-5 | cm/cm/°C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 85 到 95 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.040 | % | ||
| Suggested injection volume | 40 到 80 | % | ||
| Temperature at the rear of the barrel | 230 到 250 | °C | ||
| Temperature in the middle of the barrel | 235 到 255 | °C | ||
| Temperature at the front of the material cylinder | 245 到 260 | °C | ||
| Spray nozzle temperature | 235 到 255 | °C | ||
| Processing (melt) temperature | 255 到 270 | °C | ||
| Mold temperature | 60 到 85 | °C | ||
| Back pressure | 0.300 到 1.00 | Mpa | ||
| Screw speed | 30 到 80 | rpm | ||
| Exhaust hole depth | 0.038 到 0.076 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 30.0 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.