ASA/PC GELOY™ CR7500-GY SABIC INNOVATIVE US
230
- Unit Price:
- $3328 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Antistatic High mobility
- Application Areas:Electrical applications Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 220°C/10.0 kg | ASTM D1238 | 6.3 | g/10 min |
| 260°C/5.0 kg | ASTM D1238 | 11 | g/10 min | |
| Molten Volume Flow Rate (MVR) | 220°C/10.0 kg | ISO 1133 | 6.00 | cm3/10min |
| 260°C/5.0 kg | ISO 1133 | 10.0 | cm3/10min | |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.80 | % |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.50 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.20 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | -- 2 | ASTM D638 | 1970 | Mpa |
| -- | ISO 527-2/1 | 2040 | Mpa | |
| Tensile strength | Yield 3 | ASTM D638 | 40.0 | Mpa |
| Yield | ISO 527-2/5 | 43.0 | Mpa | |
| Break 3 | ASTM D638 | 33.0 | Mpa | |
| Break | ISO 527-2/5 | 35.0 | Mpa | |
| elongation | Yield 3 | ASTM D638 | 3.6 | % |
| Yield | ISO 527-2/5 | 3.3 | % | |
| Break 3 | ASTM D638 | 60 | % | |
| Break | ISO 527-2/5 | 19 | % | |
| Bending modulus | 50.0 mm Span 4 | ASTM D790 | 2170 | Mpa |
| -- 5 | ISO 178 | 2060 | Mpa | |
| Bending stress | -- 5, 6 | ISO 178 | 64.0 | Mpa |
| Yield, 50.0 mm Span 4 | ASTM D790 | 68.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal deformation temperature under load | 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 90.0 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 9 | ISO 75-2/Ae | 88.0 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8 | ISO 75-2/Af | 89.0 | °C | |
| Vicat softening temperature | -- | ASTM D152510 | 98.0 | °C |
| -- | ISO 306/B50 | 102 | °C | |
| -- | ISO 306/B120 | 105 | °C | |
| Ball Pressure Test | 98°C | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831, ISO 11359-2 | 8.4E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 9.5E-5 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 9.5E-5 | cm/cm/°C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 85 到 95 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.040 | % | ||
| Suggested injection volume | 40 到 80 | % | ||
| Temperature at the rear of the barrel | 230 到 250 | °C | ||
| Temperature in the middle of the barrel | 235 到 255 | °C | ||
| Temperature at the front of the material cylinder | 245 到 260 | °C | ||
| Spray nozzle temperature | 235 到 255 | °C | ||
| Processing (melt) temperature | 255 到 270 | °C | ||
| Mold temperature | 60 到 85 | °C | ||
| Back pressure | 0.300 到 1.00 | Mpa | ||
| Screw speed | 30 到 80 | rpm | ||
| Exhaust hole depth | 0.038 到 0.076 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 30.0 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.