Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.25 | |
| Molding shrinkage rate | | ASTM D955 | MD 0.1～0.4 | % |
| Water absorption rate 23 ℃/24h | | ASTM D570/ISO 62 | 0.01 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | TD | 内部方法 | 0.50to0.80 | % |
| Shrinkage rate | MD | 内部方法 | 0.10to0.40 | % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.010 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | 断裂 | ISO527-2 | 120 | Mpa |
| Tensile strain | 断裂 | ISO527-2 | 2.1 | % |
| Bending stress | | ISO178 | 185 | Mpa |
| elongation at break | | ASTM D638/ISO 527 | 2.1 | % |
| Tensile modulus | | ISO527-2 | 9700 | Mpa |
| tensile strength | | ASTM D638/ISO 527 | 120 | kg/cm²(MPa)[Lb/in²] |
| elongation | 断裂 | | 2.3 | % |
| Rockwell hardness | | ASTM D785 | 70 | |
| Bending modulus | | ASTM D790/ISO 178 | 9.2 | kg/cm²(MPa)[Lb/in²] |
| Bending modulus | | ISO178 | 9200 | Mpa |
| bending strength | | ASTM D790/ISO 178 | 185 | kg/cm²(MPa)[Lb/in²] |
| Flexural modulus of elasticity | | | 8100 | Mpa |
| Flexural strength | | | 165 | Mpa |
| Tensile strength | | | 105 | Mpa |
| IZOD impact strength | 3.2mm 没有Notch | | 40 | KJ/m |
| IZOD impact strength | 4mm 有Notch | | 10 | KJ/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Combustibility | 1/32英寸 | UL 94 | HB | |
| Linear coefficient of thermal expansion | MD：-30到30°C | TMA | 1.8E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：-30to30°C | TMA | 3.9E-05 | cm/cm/°C |
| RTIElec | | UL746 | 50.0 | °C |
| Evolution Calendar intelligent importer | | UL746 | 50.0 | °C |
| RTIStr | | UL746 | 50.0 | °C |
| Combustibility (rate) | | UL94 | HB/0.80 | |
| Hot deformation temperature | | | 235 | °C |
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 265 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 240 | °C |
| Linear expansion coefficient | | ASTM D696/ISO 11359 | MD 1.8 | mm/mm.℃ |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric constant | 1MHz | IEC60250 | 2.90 | |
| Arc resistance | | ASTMD495 | PLC6 | |
| Arc resistance | | ASTM D495/IEC 60112 | 120 | |
| Volume resistivity | | ASTM D257/IEC 60093 | >1.0*10^16 | Ω.cm |
| Volume resistivity | | IEC60093 | >1.0E+16 | ohms·cm |
| Dissipation factor | 1MHz | IEC60250 | <1.0E-3 | |
| Compared to the anti leakage trace index | CTI)3 | IEC60112 | PLC1 | |
| Dielectric strength | | ASTMD149 | 45 | KV/mm |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD | | 0.35 | % |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Unscented Izod impact strength | 23°C | ISO180 | 36 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 43 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| FlameRating | >0.75mm | UL94 | HB | |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | | | 0.05 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.