Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
SPS C132 IDEMITSU JAPAN
XAREC™
Household goods
enhance、Glass fiber reinforced、High temperature resistan
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
SPS/IDEMITSU JAPAN/C132
Molding shrinkage rate
ASTM D955
%
M
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
0
physical property
Test Condition
Test Method
Unit
SPS/IDEMITSU JAPAN/C132
Shrinkage rate
TD
内部方法
%
0
Shrinkage rate
MD
内部方法
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
SPS/IDEMITSU JAPAN/C132
elongation at break
ASTM D638/ISO 527
%
2
Tensile modulus
ISO527-2
Mpa
9
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
1
Tensile strain
断裂
ISO527-2
%
2
Tensile stress
断裂
ISO527-2
Mpa
1
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
9
Bending modulus
ISO178
Mpa
9
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
Bending stress
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
SPS/IDEMITSU JAPAN/C132
RTIElec
UL746
°C
5
Evolution Calendar intelligent importer
UL746
°C
5
RTIStr
UL746
°C
5
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Linear coefficient of thermal expansion
MD：-30到30°C
TMA
cm/cm/°C
1
Linear coefficient of thermal expansion
TD：-30to30°C
TMA
cm/cm/°C
3
Linear expansion coefficient
ASTM D696/ISO 11359
mm/mm.℃
M
Electrical performance
Test Condition
Test Method
Unit
SPS/IDEMITSU JAPAN/C132
Dielectric strength
ASTMD149
KV/mm
4
Volume resistivity
ASTM D257/IEC 60093
Ω.cm
>
Volume resistivity
IEC60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
SPS/IDEMITSU JAPAN/C132
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
4
Unscented Izod impact strength
23°C
ISO180
kJ/m²
3