PC PANLITE® AD-5503 TEIJIN JAPAN
226
- Properties:transparentHigh mobility
- Usages:Optical level
- Certificates:SGS
Compare
View PricesTechnical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | /1200 | ||
| Molding shrinkage rate | ASTM D955 | 0.5-0.7 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.2 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD:4.00mm | 内部方法 | 0.50to0.70 | % |
| MD:4.00mm | 内部方法 | 0.50to0.70 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.20 | % |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 54.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile yield elongation | 50mm/min | ISO 527-1 and ISO 527-2 | 6 | % |
| Izod notched impact strength | 没缺口 | ISO 179 | NB | KJ/m |
| 带缺口 | ISO 179 | 3 | KJ/m | |
| Tensile fracture nominal elongation | 50mm/min | ISO 527-1 and ISO 527-2 | >50 | % |
| Tensile stress | 屈服 | ISO527-2/50 | 63.0 | Mpa |
| Tensile strain | 屈服 | ISO527-2/50 | 6.0 | % |
| 断裂 | ISO527-2/50 | >50 | % | |
| Tensile yield stress | 50mm/min | ISO 527-1 and ISO 527-2 | 63 | Mpa |
| Bending modulus 2 | ISO178 | 2400 | Mpa | |
| Bending stress 2 | ISO178 | 96.0 | Mpa | |
| Tensile modulus | ASTM D638/ISO 527 | /2450 | kg/cm²(MPa)[Lb/in²] | |
| 1mm/min | ISO 527-1 and ISO 527-2 | 2450 | Mpa | |
| ISO527-2/1 | 2450 | Mpa | ||
| tensile strength | ASTM D638/ISO 527 | /63 | kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | /6 | % | |
| Bending modulus | ASTM D790/ISO 178 | /2400 | kg/cm²(MPa)[Lb/in²] | |
| 2mm/min | ISO 178 | 2400 | Mpa | |
| bending strength | 2mm/min | ISO 178 | 96 | Mpa |
| ASTM D790/ISO 178 | /96 | kg/cm²(MPa)[Lb/in²] |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 138 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 124 | °C | |
| vicat softening point | ASTM D1525/ISO R306 | 143 | ℃（℉） | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.7 | mm/mm.℃ | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 7E-05 | cm/cm/°C |
| TD | ISO11359-2 | 7E-05 | cm/cm/°C | |
| Vicat softening temperature | ISO306/B50 | 143 | °C | |
| Vicat softening point | 50℃/h 50N | ISO 308 | 143 | °C |
| heat deflection temperature | 0.45MPa | ISO 75-1 and ISO 75-2 | 138 | °C |
| 1.80MPa | ISO 75-1 and ISO 75-2 | 124 | °C | |
| Coefficient of linear expansion | 垂直方向 | ISO 11359-2 | 0.7 | X10 |
| 平行方向 | ISO 11359-2 | 0.7 | X10 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative permittivity | 100Hz | IEC60250 | 3.10 | |
| 1MHz | IEC60250 | 3.00 | ||
| Leakage Trace Index | IEC60112 | 250 | V | |
| Voltage endurance | 短时间法 | IEO 60243-1 | 30 | MV/m |
| Dielectric strength 3 | IEC60243-1 | 30 | KV/mm | |
| dielectric loss tangent | 1MHz | IEO 60250 | 90 | X10 |
| 100Hz | IEO 60250 | 10 | X10 | |
| Dissipation factor | 100Hz | IEC60250 | 1E-03 | |
| 1MHz | IEC60250 | 9E-03 | ||
| Surface resistivity | IEO 60250 | >1×10 | Ω | |
| IEC60093 | >1.0E+15 | ohms | ||
| Dielectric constant | 100Hz | IEO 60250 | 3.1 | |
| 1MHz | IEO 60250 | 3 | ||
| ASTM D150/IEC 60250 | 3.1 | |||
| ASTM D150/IEC 60250 | 3 | |||
| Arc resistance | IEO 60112 | 250 | ||
| Volume resistivity | IEO 60250 | >1×10 | Ω.cm | |
| IEC60093 | >1.0E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179 | NoBreak |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Light transmittance | ASTM D1003/ISO 13468 | 89 | % | |
| Refractive index | ASTM D542/ISO 489 | 1.585 | ||
| ASTMD542 | 1.585 | |||
| transmissivity | 3000µm | ASTMD1003 | 89.0 | % |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting volume flow rate | 300℃负荷1.2kg | ISO1133 | 54 | CM |
| Refractive index | ASTM D542 | 1.585 | ||
| Light transmittance | 试样厚度3mm | ASTM D1003 | 89 | % |
| density | ISO 1183 | 1200 | kg/m | |
| Shrinkage rate | 垂直方向 | 本公司制订的测定法 | 0.5-0.7 | % |
| 平行方向 | 本公司制订的测定法 | 0.5-0.7 | % | |
| Water absorption rate | 放置在23℃水中24h | ISO 62 | 0.2 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.