PC PANLITE® AD-5503 TEIJIN JAPAN
232
- Unit Price:
- $5294 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 61.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:transparent High mobility
- Application Areas:Optical level
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | /1200 | ||
| Molding shrinkage rate | ASTM D955 | 0.5-0.7 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.2 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 54.0 | cm3/10min |
| Shrinkage rate | TD:4.00mm | 内部方法 | 0.50to0.70 | % |
| MD:4.00mm | 内部方法 | 0.50to0.70 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.20 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2/1 | 2450 | Mpa | |
| Tensile stress | Yield | ISO527-2/50 | 63.0 | Mpa |
| Tensile strain | Yield | ISO527-2/50 | 6.0 | % |
| Break | ISO527-2/50 | >50 | % | |
| Bending modulus 2 | ISO178 | 2400 | Mpa | |
| Bending stress 2 | ISO178 | 96.0 | Mpa | |
| Tensile modulus | ASTM D638/ISO 527 | /2450 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | /63 | kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | /6 | % | |
| Bending modulus | ASTM D790/ISO 178 | /2400 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | /96 | kg/cm²(MPa)[Lb/in²] | |
| Tensile yield elongation | 50mm/min | ISO 527-1 and ISO 527-2 | 6 | % |
| Izod notched impact strength | 没Notched | ISO 179 | NB | KJ/m |
| Tensile yield stress | 50mm/min | ISO 527-1 and ISO 527-2 | 63 | Mpa |
| Bending modulus | 2mm/min | ISO 178 | 2400 | Mpa |
| bending strength | 2mm/min | ISO 178 | 96 | Mpa |
| Tensile fracture nominal elongation | 50mm/min | ISO 527-1 and ISO 527-2 | >50 | % |
| Izod notched impact strength | 带Notched | ISO 179 | 3 | KJ/m |
| Tensile modulus | 1mm/min | ISO 527-1 and ISO 527-2 | 2450 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| heat deflection temperature | 1.80MPa | ISO 75-1 and ISO 75-2 | 124 | °C |
| Coefficient of linear expansion | Flow | ISO 11359-2 | 0.7 | X10 |
| heat deflection temperature | 0.45MPa | ISO 75-1 and ISO 75-2 | 138 | °C |
| vicat softening point | ASTM D1525/ISO R306 | 143 | ℃（℉） | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.7 | mm/mm.℃ | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 138 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 124 | °C | |
| Vicat softening temperature | ISO306/B50 | 143 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 7E-05 | cm/cm/°C |
| TD | ISO11359-2 | 7E-05 | cm/cm/°C | |
| Vicat softening point | 50℃/h 50N | ISO 308 | 143 | °C |
| Coefficient of linear expansion | Across Flow | ISO 11359-2 | 0.7 | X10 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric constant | ASTM D150/IEC 60250 | 3.1 | ||
| ASTM D150/IEC 60250 | 3 | |||
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric constant | 100Hz | IEO 60250 | 3.1 | |
| 1MHz | IEO 60250 | 3 | ||
| Volume resistivity | IEO 60250 | >1×10 | Ω.cm | |
| Voltage endurance | 短时间法 | IEO 60243-1 | 30 | MV/m |
| dielectric loss tangent | 1MHz | IEO 60250 | 90 | X10 |
| Arc resistance | IEO 60112 | 250 | ||
| dielectric loss tangent | 100Hz | IEO 60250 | 10 | X10 |
| Surface resistivity | IEO 60250 | >1×10 | Ω | |
| Dielectric strength 3 | IEC60243-1 | 30 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 3.10 | |
| 1MHz | IEC60250 | 3.00 | ||
| Dissipation factor | 100Hz | IEC60250 | 1E-03 | |
| 1MHz | IEC60250 | 9E-03 | ||
| Leakage Trace Index | IEC60112 | 250 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179 | NoBreak |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ASTMD542 | 1.585 | ||
| transmissivity | 3000µm | ASTMD1003 | 89.0 | % |
| Light transmittance | ASTM D1003/ISO 13468 | 89 | % | |
| Refractive index | ASTM D542/ISO 489 | 1.585 |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ISO 1183 | 1200 | kg/m | |
| Water absorption rate | 放置在23℃水中24h | ISO 62 | 0.2 | % |
| Melting volume flow rate | 300℃负荷1.2kg | ISO1133 | 54 | CM |
| Shrinkage rate | Flow | 本公司制订的测定法 | 0.5-0.7 | % |
| Refractive index | ASTM D542 | 1.585 | ||
| Light transmittance | 试样厚度3mm | ASTM D1003 | 89 | % |
| Shrinkage rate | Across Flow | 本公司制订的测定法 | 0.5-0.7 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.