PBT VALOX™ 310SE0-BK SABIC INNOVATIVE US
402
- Properties:Flame retardant
- Usages:Electrical fieldElectronic fieldHome appliance componentsswitchShellSpool
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：--2 | 内部方法 | 1.1to1.8 | % |
| MD：--3 | 内部方法 | 1.5to2.3 | % | |
| MD：--4 | 内部方法 | 0.90to1.6 | % | |
| MD：3.20mm | 内部方法 | 1.5to2.3 | % | |
| TD：--2 | 内部方法 | 0.90to1.9 | % | |
| TD：--4 | 内部方法 | 1.0to1.7 | % | |
| TD：--3 | 内部方法 | 1.6to2.4 | % | |
| Water absorption rate | 饱和,23°C | ISO62 | 0.36 | % |
| 平衡,23°C,50%RH | ISO62 | 0.080 | % | |
| Melt mass flow rate | 250°C/2.16kg | ASTMD1238 | 8.6 | g/10min |
| Melt volume flow rate | 250°C/2.16kg | ISO1133 | 8.00 | cm3/10min |
| Density/specific gravity | ASTMD792 | 1.40 | g/cm³ | |
| ISO1183 | 1.40 | g/cm³ | ||
| Specific volume | ASTMD792 | 0.710 | cm³/g |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending modulus 7 | 50.0mmSpan | ASTMD790 | 2620 | Mpa |
| Bending strength 8,9 | ISO178 | 90.0 | Mpa | |
| Tensile strain 6 | Yield | ASTMD638 | 20 | % |
| Bending modulus 8 | ISO178 | 2600 | Mpa | |
| Tensile strength 6 | Break | ASTMD638 | 58.0 | Mpa |
| Yield | ASTMD638 | 58.0 | Mpa | |
| Elongation rate 6 | 断裂 | ASTMD638 | 20 | % |
| FlexuralStrength7 | Yield,50.0mmSpan | ASTMD790 | 101 | Mpa |
| Tensile modulus 5 | ASTMD638 | 2820 | Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 19.0 | mg |
| Tensile stress | 屈服 | ISO527-2/50 | 55.0 | Mpa |
| 断裂 | ISO527-2/50 | 40.0 | Mpa | |
| Tensile strain | 屈服 | ISO527-2/50 | 6.0 | % |
| 断裂 | ISO527-2/50 | 20 | % | |
| Tensile modulus | ISO527-2/1 | 2800 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,未退火,100mm跨距12 | ISO75-2/Ae | 60.0 | °C |
| 1.8MPa,未退火,64.0mm跨距13 | ISO75-2/Af | 71.0 | °C | |
| 0.45MPa,未退火,6.40mm | ASTMD648 | 162 | °C | |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 74.0 | °C | |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 71.0 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 7.9E-05 | cm/cm/°C |
| MD：60to138°C | ASTME831 | 1.3E-04 | cm/cm/°C | |
| MD：-40to40°C | ISO11359-2 | 7.6E-05 | cm/cm/°C | |
| MD：23to60°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 7.9E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 7.3E-05 | cm/cm/°C | |
| TD：23to60°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| RTIElec | UL746 | 120 | °C | |
| Evolution Calendar intelligent importer | UL746 | 120 | °C | |
| RTIStr | UL746 | 140 | °C | |
| thermal conductivity | ISO8302 | 0.24 | W/m/K | |
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| Vicat softening temperature | ASTMD152514 | 165 | °C | |
| -- | ISO306/A50 | 212 | °C | |
| -- | ISO306/B50 | 165 | °C | |
| -- | ISO306/B120 | 165 | °C | |
| Hot deformation temperature 12 | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 135 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| High arc combustion index | HAI | UL746 | PLC0 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC4 | |
| High voltage arc ignition resistance index | PLC | UL746 | PLC6 | |
| Compared to the anti leakage trace index | CTI | UL746 | PLC3 | |
| Hot wire ignition | HWI | UL746 | PLC2 | |
| Arc resistance 16 | ASTMD495 | PLC6 | ||
| Relative permittivity | 50Hz | IEC60250 | 2.90 | |
| 60Hz | IEC60250 | 2.90 | ||
| 100Hz | IEC60250 | 3.10 | ||
| 1MHz | IEC60250 | 2.80 | ||
| Leakage Trace Index | -- | IEC60112 | 175 | V |
| 解决方案B | IEC60112 | 100 | V | |
| Dissipation factor | 50Hz | IEC60250 | 1E-03 | |
| 60Hz | IEC60250 | 1E-03 | ||
| 100Hz | IEC60250 | 2E-03 | ||
| 1MHz | IEC60250 | 0.010 | ||
| Dielectric strength | 1.60mm,在油中 | ASTMD149 | 22 | KV/mm |
| 3.20mm,inAir | ASTMD149 | 18 | KV/mm | |
| 0.800mm,在油中 | IEC60243-1 | 31 | KV/mm | |
| 1.00mm15 | IEC60243-1 | 18 | KV/mm | |
| 1.60mm,在油中 | IEC60243-1 | 24 | KV/mm | |
| 3.20mm,在油中 | IEC60243-1 | 15 | KV/mm | |
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 200 | J |
| Suspended wall beam gap impact strength 11 | -30°C | ISO180/1A | 3.0 | kJ/m² |
| 23°C | ISO180/1A | 5.0 | kJ/m² | |
| Unscented Izod Impact Strength 11 | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak | ||
| Charpy Notched Impact Strength | 23°C10 | ISO179/1eA | 8.0 | kJ/m² |
| 23°C | ISO179/2C | 4.0 | kJ/m² | |
| -30°C10 | ISO179/1eA | 4.0 | kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ASTMD4812 | 1600 | J/m |
| -30°C | ASTMD256 | 22 | J/m | |
| 23°C | ASTMD256 | 37 | J/m | |
| The impact strength of a simply supported beam without a notch is 10 | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R级 | ISO2039-2 | 120 | |
| Ball pressure hardness | H358/30 | ISO2039-1 | 105 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.71mm | UL94 | V-0 | |
| 3.0mm | UL94 | 5VA | ||
| Burning wire flammability index | 1.0mm | IEC60695-2-12 | 960 | °C |
| Extreme Oxygen Index | ISO4589-2 | 30 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.