PBT VALOX™ 310SE0-BK SABIC INNOVATIVE US
141
- Unit Price:
- $3136 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant
- Application Areas:Electrical field Electronic field Home appliance components switch Shell Spool
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ASTMD792 | 1.40 | g/cm³ | |
| Specific volume | ASTMD792 | 0.710 | cm³/g | |
| Density/specific gravity | ISO1183 | 1.40 | g/cm³ | |
| Melt mass flow rate | 250°C/2.16kg | ASTMD1238 | 8.6 | g/10min |
| Melt volume flow rate | 250°C/2.16kg | ISO1133 | 8.00 | cm3/10min |
| Shrinkage rate | MD：--2 | 内部方法 | 1.1to1.8 | % |
| MD：--3 | 内部方法 | 1.5to2.3 | % | |
| MD：--4 | 内部方法 | 0.90to1.6 | % | |
| MD：3.20mm | 内部方法 | 1.5to2.3 | % | |
| TD：--2 | 内部方法 | 0.90to1.9 | % | |
| TD：--4 | 内部方法 | 1.0to1.7 | % | |
| TD：--3 | 内部方法 | 1.6to2.4 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.36 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.080 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 5 | ASTMD638 | 2820 | Mpa | |
| Tensile modulus | ISO527-2/1 | 2800 | Mpa | |
| Tensile strength 6 | Yield | ASTMD638 | 58.0 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 55.0 | Mpa |
| Tensile strength 6 | Break | ASTMD638 | 58.0 | Mpa |
| Tensile stress | Break | ISO527-2/50 | 40.0 | Mpa |
| Tensile strain 6 | Yield | ASTMD638 | 20 | % |
| Tensile strain | Yield | ISO527-2/50 | 6.0 | % |
| Elongation rate 6 | Break | ASTMD638 | 20 | % |
| Tensile strain | Break | ISO527-2/50 | 20 | % |
| Bending modulus 7 | 50.0mmSpan | ASTMD790 | 2620 | Mpa |
| Bending modulus 8 | ISO178 | 2600 | Mpa | |
| Bending strength 8,9 | ISO178 | 90.0 | Mpa | |
| FlexuralStrength7 | Yield,50.0mmSpan | ASTMD790 | 101 | Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | 内部方法 | 19.0 | mg |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,100mmSpan12 | ISO75-2/Ae | 60.0 | °C |
| 1.8MPa,Unannealed,64.0mmSpan13 | ISO75-2/Af | 71.0 | °C | |
| Vicat softening temperature | ASTMD152514 | 165 | °C | |
| -- | ISO306/A50 | 212 | °C | |
| -- | ISO306/B50 | 165 | °C | |
| -- | ISO306/B120 | 165 | °C | |
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 7.9E-05 | cm/cm/°C |
| MD：60to138°C | ASTME831 | 1.3E-04 | cm/cm/°C | |
| MD：-40to40°C | ISO11359-2 | 7.6E-05 | cm/cm/°C | |
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 162 | °C |
| Hot deformation temperature 12 | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 135 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 74.0 | °C |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 71.0 | °C | |
| Linear coefficient of thermal expansion | MD：23to60°C | ISO11359-2 | 1E-04 | cm/cm/°C |
| TD：-40to40°C | ASTME831 | 7.9E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 7.3E-05 | cm/cm/°C | |
| TD：23to60°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| thermal conductivity | ISO8302 | 0.24 | W/m/K | |
| RTIElec | UL746 | 120 | °C | |
| Evolution Calendar intelligent importer | UL746 | 120 | °C | |
| RTIStr | UL746 | 140 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| High voltage arc tracing rate | HVTR | UL746 | PLC4 | |
| Hot wire ignition | HWI | UL746 | PLC2 | |
| Dielectric strength | 1.60mm,in Oil | ASTMD149 | 22 | KV/mm |
| 3.20mm,inAir | ASTMD149 | 18 | KV/mm | |
| 0.800mm,in Oil | IEC60243-1 | 31 | KV/mm | |
| 1.00mm15 | IEC60243-1 | 18 | KV/mm | |
| 1.60mm,in Oil | IEC60243-1 | 24 | KV/mm | |
| 3.20mm,in Oil | IEC60243-1 | 15 | KV/mm | |
| Relative permittivity | 50Hz | IEC60250 | 2.90 | |
| 60Hz | IEC60250 | 2.90 | ||
| 100Hz | IEC60250 | 3.10 | ||
| 1MHz | IEC60250 | 2.80 | ||
| Dissipation factor | 50Hz | IEC60250 | 1E-03 | |
| 60Hz | IEC60250 | 1E-03 | ||
| 100Hz | IEC60250 | 2E-03 | ||
| 1MHz | IEC60250 | 0.010 | ||
| Arc resistance 16 | ASTMD495 | PLC6 | ||
| Compared to the anti leakage trace index | CTI | UL746 | PLC3 | |
| Leakage Trace Index | -- | IEC60112 | 175 | V |
| SolutionB | IEC60112 | 100 | V | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| High voltage arc ignition resistance index | PLC | UL746 | PLC6 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTMD4812 | 1600 | J/m |
| Unscented Izod Impact Strength 11 | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak | ||
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 200 | J |
| Charpy Notched Impact Strength | 23°C10 | ISO179/1eA | 8.0 | kJ/m² |
| 23°C | ISO179/2C | 4.0 | kJ/m² | |
| The impact strength of a simply supported beam without a notch is 10 | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 22 | J/m |
| 23°C | ASTMD256 | 37 | J/m | |
| Suspended wall beam gap impact strength 11 | -30°C | ISO180/1A | 3.0 | kJ/m² |
| 23°C | ISO180/1A | 5.0 | kJ/m² | |
| Charpy Notched Impact Strength | -30°C10 | ISO179/1eA | 4.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ISO2039-2 | 120 | |
| Ball pressure hardness | H358/30 | ISO2039-1 | 105 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.71mm | UL94 | V-0 | |
| 3.0mm | UL94 | 5VA | ||
| Burning wire flammability index | 1.0mm | IEC60695-2-12 | 960 | °C |
| Extreme Oxygen Index | ISO4589-2 | 30 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.