ABS CYCOLAC™ MG47F-NA1000 SABIC INNOVATIVE MEXICO
557
- Properties:High impact resistance
- Certificates:ULFDARoHS
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 230°C/3.8 kg | ASTM D1238 | 5.6 | g/10 min |
| 220°C/10.0 kg | ISO 1133 | 18 | g/10 min | |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.80 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | -- 1 | ASTM D638 | 2270 | Mpa |
| -- | ISO 527-2/1 | 2370 | Mpa | |
| elongation | 屈服 2 | ASTM D638 | 2.0 | % |
| 屈服 | ISO 527-2/50 | 2.6 | % | |
| 断裂 2 | ASTM D638 | 24 | % | |
| 断裂 | ISO 527-2/50 | 25 | % | |
| Bending modulus | 50.0 mm 跨距 3 | ASTM D790 | 2300 | Mpa |
| -- 4 | ISO 178 | 2200 | Mpa | |
| Tensile strength | 屈服 2 | ASTM D638 | 44.0 | Mpa |
| 屈服 | ISO 527-2/50 | 47.0 | Mpa | |
| 断裂 2 | ASTM D638 | 33.0 | Mpa | |
| 断裂 | ISO 527-2/50 | 35.0 | Mpa | |
| Bending stress | -- 4, 5 | ISO 178 | 70.0 | Mpa |
| 屈服, 50.0 mm 跨距 3 | ASTM D790 | 70.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTI | UL 746 | 60.0 | °C | |
| RTI Imp | UL 746 | 60.0 | °C | |
| RTI Elec | UL 746 | 60.0 | °C | |
| Vicat softening temperature | -- | 99.0 | °C | |
| -- | ISO 306/B50 | 98.0 | °C | |
| -- | ISO 306/B120 | 100 | °C | |
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 8.8E-5 | cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 8.8E-5 | cm/cm/°C | |
| Thermal deformation temperature under load | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 94.0 | °C |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 80.0 | °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7 | ISO 75-2/Af | 81.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 0 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 3 | ||
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 3 | ||
| Arc resistance 9 | ASTM D495 | PLC 6 | ||
| High arc combustion index (HAI) 10 | UL 746 | PLC 0 |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt viscosity | 240°C, 1000 sec^-1 | ASTM D3835 | 225 | Pa·s |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 到 95 | °C | ||
| Suggested maximum moisture content | 0.10 | % | ||
| Processing (melt) temperature | 220 到 260 | °C | ||
| Mold temperature | 50 到 70 | °C | ||
| drying time | 2.0 到 4.0 | hr | ||
| Suggested injection volume | 50 到 70 | % | ||
| Temperature at the rear of the barrel | 190 到 210 | °C | ||
| Temperature in the middle of the barrel | 205 到 225 | °C | ||
| Temperature at the front of the material cylinder | 215 到 240 | °C | ||
| Spray nozzle temperature | 220 到 260 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 30 到 60 | rpm | ||
| Exhaust hole depth | 0.038 到 0.051 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 30.0 | J |
| Impact strength of simply supported beam gap 6 | -30°C | ISO 179/1eA | 9.0 | kJ/m² |
| 23°C | ISO 179/1eA | 26 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R 级 | ASTM D785 | 112 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.