ABS CYCOLAC™ MG47F-NA1000 SABIC INNOVATIVE MEXICO
153
Unit Price:$1895 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 熔流率（熔体流动速率） | 230°C/3.8 kg | ASTM D1238 | 5.6 | g/10 min |
| 220°C/10.0 kg | ISO 1133 | 18 | g/10 min | |
| 收缩率 - 流动 | 3.20 mm | 内部方法 | 0.50 到 0.80 | % |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 拉伸模量 | -- 1 | ASTM D638 | 2270 | Mpa |
| -- | ISO 527-2/1 | 2370 | Mpa | |
| 抗张强度 | 屈服 2 | ASTM D638 | 44.0 | Mpa |
| 屈服 | ISO 527-2/50 | 47.0 | Mpa | |
| 断裂 2 | ASTM D638 | 33.0 | Mpa | |
| 断裂 | ISO 527-2/50 | 35.0 | Mpa | |
| 伸长率 | 屈服 2 | ASTM D638 | 2.0 | % |
| 屈服 | ISO 527-2/50 | 2.6 | % | |
| 断裂 2 | ASTM D638 | 24 | % | |
| 断裂 | ISO 527-2/50 | 25 | % | |
| 弯曲模量 | 50.0 mm 跨距 3 | ASTM D790 | 2300 | Mpa |
| -- 4 | ISO 178 | 2200 | Mpa | |
| 弯曲应力 | -- 4, 5 | ISO 178 | 70.0 | Mpa |
| 屈服, 50.0 mm 跨距 3 | ASTM D790 | 70.0 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 载荷下热变形温度 | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 94.0 | °C |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 80.0 | °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7 | ISO 75-2/Af | 81.0 | °C | |
| 维卡软化温度 | -- | 99.0 | °C | |
| -- | ISO 306/B50 | 98.0 | °C | |
| -- | ISO 306/B120 | 100 | °C | |
| 线形热膨胀系数 | 流动 : -40 到 40°C | ASTM E831 | 8.8E-5 | cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 8.8E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | 60.0 | °C | |
| RTI Imp | UL 746 | 60.0 | °C | |
| RTI | UL 746 | 60.0 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 耐电弧性 9 | ASTM D495 | PLC 6 | ||
| 相比耐漏电起痕指数(CTI) | UL 746 | PLC 0 | ||
| 高电弧燃烧指数(HAI) 10 | UL 746 | PLC 0 | ||
| 高电压电弧起痕速率 (HVTR) | UL 746 | PLC 3 | ||
| 热丝引燃 (HWI) | UL 746 | PLC 3 |
| 充模分析 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 熔体粘度 | 240°C, 1000 sec^-1 | ASTM D3835 | 225 | Pa·s |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥温度 | 80 到 95 | °C | ||
| 干燥时间 | 2.0 到 4.0 | hr | ||
| 建议的最大水分含量 | 0.10 | % | ||
| 建议注射量 | 50 到 70 | % | ||
| 料筒后部温度 | 190 到 210 | °C | ||
| 料筒中部温度 | 205 到 225 | °C | ||
| 料筒前部温度 | 215 到 240 | °C | ||
| 射嘴温度 | 220 到 260 | °C | ||
| 加工（熔体）温度 | 220 到 260 | °C | ||
| 模具温度 | 50 到 70 | °C | ||
| 背压 | 0.300 到 0.700 | Mpa | ||
| 螺杆转速 | 30 到 60 | rpm | ||
| 排气孔深度 | 0.038 到 0.051 | mm |
| 冲击性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 简支梁缺口冲击强度 6 | -30°C | ISO 179/1eA | 9.0 | kJ/m² |
| 23°C | ISO 179/1eA | 26 | kJ/m² | |
| 装有测量仪表的落镖冲击 | 23°C, Total Energy | ASTM D3763 | 30.0 | J |
| 硬度 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 洛氏硬度 | R 级 | ASTM D785 | 112 |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL 阻燃等级 | 1.5 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.