Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | | ASTMD792 | 1.68 | g/cm³ |
| Melt mass flow rate | 275°C/2.16kg | ASTMD1238 | 0.90到1.3 | g/10min |
| Shrinkage rate | MD | ASTMD955 | 2.5 | % |
| Water absorption rate | 平衡 | ASTMD570 | <0.10 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| friction coefficient | 泰伯耐磨性(1000Cycles,500g,CS-17转轮) | ASTMD1894 | 5.00 | mg |
| Tensile modulus 2 | 23°C | ASTMD638 | 1660 | Mpa |
| Tensile strength 2 | 屈服,23°C | ASTMD638 | 30.0 | Mpa |
| Tensile strength 2 | 断裂,23°C | ASTMD638 | 54.0 | Mpa |
| Elongation rate 2 | 屈服,23°C | ASTMD638 | 5.0 | % |
| Elongation rate 2 | 断裂,23°C | ASTMD638 | 250 | % |
| Bending modulus 3 | 23°C | ASTMD790 | 1690 | Mpa |
| Bending strength 3 | 23°C | ASTMD790 | 47.0 | Mpa |
| friction coefficient | 与自身-动态 | ASTMD1894 | 0.20 | |
| friction coefficient | 与自身-静态 | ASTMD1894 | 0.20 | |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| specific heat | 23°C | ASTMD3418 | 962 | J/kg/°C |
| thermal conductivity | 40°C | ASTMC177 | 0.15 | W/m/K |
| Crystallization heat | | ASTMD3418 | 40.0 | J/g |
| Thermal stability -1% mass loss, N2 | | TGA | 405 | °C |
| Fusion heat | | ASTMD3418 | 42.0 | J/g |
| Hot deformation temperature | 0.45MPa,未退火 | ASTMD648 | 90.0 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ASTMD648 | 65.0 | °C |
| Brittle temperature | | ASTMD746A | <-76.0 | °C |
| Glass transition temperature | | DMA | 85.0 | °C |
| Melting temperature | | ASTMD3418 | 242 | °C |
| Crystallization peak temperature | DSC | ASTMD3418 | 222 | °C |
| Linear coefficient of thermal expansion | MD | ASTMD696 | 1E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity 4 | 23°C | ASTMD257 | 5.5E+16 | ohms·cm |
| Dielectric strength | 23°C,3.20mm | ASTMD149 | 14 | KV/mm |
| Dielectric constant | 23°C,1MHz | ASTMD150 | 2.57 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | -40°C,3.20mm | ASTMD256 | 210 | J/m |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTMD256 | 无断裂 | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore hardness | 邵氏D | ASTMD2240 | 75 | |
| Rockwell hardness | R级 | ASTMD785 | 90 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | V-0 | |
| Extreme Oxygen Index | | ASTMD2863 | 52 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.