Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD | ASTMD955 | 2.5 | % |
| Water absorption rate | Equilibrium | ASTMD570 | <0.10 | % |
| Melt mass flow rate | 275°C/2.16kg | ASTMD1238 | 0.90到1.3 | g/10min |
| Density/specific gravity | | ASTMD792 | 1.68 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending modulus 3 | 23°C | ASTMD790 | 1690 | Mpa |
| Tensile modulus 2 | 23°C | ASTMD638 | 1660 | Mpa |
| friction coefficient | Itself - Dynamic | ASTMD1894 | 0.20 | |
| friction coefficient | Itself - Static | ASTMD1894 | 0.20 | |
| friction coefficient | 泰伯耐磨性(1000Cycles,500g,CS-17Wheel) | ASTMD1894 | 5.00 | mg |
| Tensile strength 2 | Yield,23°C | ASTMD638 | 30.0 | Mpa |
| Tensile strength 2 | Break,23°C | ASTMD638 | 54.0 | Mpa |
| Elongation rate 2 | Yield,23°C | ASTMD638 | 5.0 | % |
| Elongation rate 2 | Break,23°C | ASTMD638 | 250 | % |
| Bending strength 3 | 23°C | ASTMD790 | 47.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear coefficient of thermal expansion | MD | ASTMD696 | 1E-04 | cm/cm/°C |
| Melting temperature | | ASTMD3418 | 242 | °C |
| Brittle temperature | | ASTMD746A | <-76.0 | °C |
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 90.0 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed | ASTMD648 | 65.0 | °C |
| specific heat | 23°C | ASTMD3418 | 962 | J/kg/°C |
| thermal conductivity | 40°C | ASTMC177 | 0.15 | W/m/K |
| Glass transition temperature | | DMA | 85.0 | °C |
| Crystallization peak temperature | DSC | ASTMD3418 | 222 | °C |
| Fusion heat | | ASTMD3418 | 42.0 | J/g |
| Crystallization heat | | ASTMD3418 | 40.0 | J/g |
| Thermal stability -1% mass loss, N2 | | TGA | 405 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity 4 | 23°C | ASTMD257 | 5.5E+16 | ohms·cm |
| Dielectric constant | 23°C,1MHz | ASTMD150 | 2.57 | |
| Dielectric strength | 23°C,3.20mm | ASTMD149 | 14 | KV/mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | -40°C,3.20mm | ASTMD256 | 210 | J/m |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTMD256 | 无断裂 | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 90 | |
| Shore hardness | Shore D | ASTMD2240 | 75 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | V-0 | |
| Extreme Oxygen Index | | ASTMD2863 | 52 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.