PA6 Zytel® 73G15HSL BK363 DUPONT USA
384
- Properties:Thermal stabilityHigh crystallinity
- Usages:Industrial machineryAutomotive components
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.25 |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ThermalConductivityofMelt | 0.20 | W/m/K | ||
| Shrinkage rate | TD | ISO294-4 | 0.80 | % |
| MD | ISO294-4 | 0.30 | % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 7.6 | % |
| 平衡,23°C,2.00mm,50%RH | ISO62 | 2.5 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2 | 130 | Mpa |
| Tensile strain | 断裂 | ISO527-2 | 2.3 | % |
| elongation at break | ASTM D638/ISO 527 | 2.3 | % | |
| Tensile modulus | ASTM D638/ISO 527 | 6500 | kg/cm²(MPa)[Lb/in²] | |
| ISO527-2 | 6500 | Mpa | ||
| tensile strength | ASTM D638/ISO 527 | 130 | kg/cm²(MPa)[Lb/in²] | |
| Charpy impact strength | ASTM D256/ISO 179 | 6 | kg·cm/cm(J/M)ft·lb/in | |
| IZOD notch impact strength | ASTM D256/ISO 179 | 40 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature 2 | ISO11357-3 | 221 | °C | |
| Vicat softening temperature | ISO306/B50 | 215 | °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 1.6E-05 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 3.5E-05 | cm/cm/°C | |
| MD：55to160°C | ISO11359-2 | 1.5E-05 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 9E-05 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 7.8E-05 | cm/cm/°C | |
| TD：55to160°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| Combustibility (rate) | UL94 | HB | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 204 | ℃（℉） | |
| 0.45MPa,未退火 | ISO75-2/B | 220 | °C | |
| 1.8MPa,未退火 | ISO75-2/A | 204 | °C | |
| melting point | 221 | ℃（℉） |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | IEC60243-1 | 22 | KV/mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 40 | kJ/m² |
| 23°C | ISO179/1eU | 40 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| Extreme Oxygen Index | ISO4589-2 | 21 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| Fogging-G-value | condensate | ISO6452 | 0.0 | g |
| Burning rate 3 | 1.00mm | ISO3795 | 25 | mm/min |
| Flammability level | 1.5mm | IEC60695-11-10,-20 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Odor4 | VDA270 | 4.00 | ||
| EmissionofOrganicCompounds4 | VDA277 | 8.50 | µgC/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.