PA6 Zytel® 73G15HSL BK363 DUPONT USA
145
- Unit Price:
- $2953 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 132.35MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability High crystallinity
- Application Areas:Industrial machinery Automotive components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.25 |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 0.80 | % |
| MD | ISO294-4 | 0.30 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 7.6 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 2.5 | % | |
| ThermalConductivityofMelt | 0.20 | W/m/K |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| elongation at break | ASTM D638/ISO 527 | 2.3 | % | |
| Tensile modulus | ASTM D638/ISO 527 | 6500 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 130 | kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO527-2 | 6500 | Mpa | |
| Tensile stress | Break | ISO527-2 | 130 | Mpa |
| Tensile strain | Break | ISO527-2 | 2.3 | % |
| Charpy impact strength | ASTM D256/ISO 179 | 6 | kg·cm/cm(J/M)ft·lb/in | |
| IZOD notch impact strength | ASTM D256/ISO 179 | 40 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | HB | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 204 | ℃（℉） | |
| melting point | 221 | ℃（℉） | ||
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 220 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 204 | °C | |
| Vicat softening temperature | ISO306/B50 | 215 | °C | |
| Melting temperature 2 | ISO11357-3 | 221 | °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 1.6E-05 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 3.5E-05 | cm/cm/°C | |
| MD：55to160°C | ISO11359-2 | 1.5E-05 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 9E-05 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 7.8E-05 | cm/cm/°C | |
| TD：55to160°C | ISO11359-2 | 1E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | IEC60243-1 | 22 | KV/mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 40 | kJ/m² |
| 23°C | ISO179/1eU | 40 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning rate 3 | 1.00mm | ISO3795 | 25 | mm/min |
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| Flammability level | 1.5mm | IEC60695-11-10,-20 | HB | |
| Extreme Oxygen Index | ISO4589-2 | 21 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| Fogging-G-value | condensate | ISO6452 | 0.0 | g |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds4 | VDA277 | 8.50 | µgC/g | |
| Odor4 | VDA270 | 4.00 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.