Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | 23°C,24hr | ISO62 | 0.70 | % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 0.70 | % |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.30 | % |
| Shrinkage rate | TD | ISO294-4 | 0.80 | % |
| Shrinkage rate | MD | ISO294-4 | 0.80 | % |
| MediumDensity | | | 1.10 | g/cm³ |
| Melt volume flow rate | 220°C/2.16kg | ISO1133 | 8.80 | cm3/10min |
| Melt mass flow rate | 220°C/2.16kg | ISO1133 | 8.5 | g/10min |
| Density/specific gravity | | ISO1183 | 1.11 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Nominal tensile fracture strain | | ISO527-2 | 800 | % |
| Tensile modulus | | ISO527-2 | 45.0 | Mpa |
| Bending modulus | | ISO178 | 45.0 | Mpa |
| Tensile stress | 10%应变 | ISO527-2 | 3.20 | Mpa |
| Tensile stress | 50%应变 | ISO527-2 | 6.70 | Mpa |
| Tensile stress | 断裂 | ISO527-2 | 29.0 | Mpa |
| Tensile strain | 断裂 | ISO527-2 | >300 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Brittle temperature | | ISO974 | -96.0 | °C |
| Glass transition temperature 2 | | ISO11357-2 | -50.0 | °C |
| Linear coefficient of thermal expansion | TD：-40to23°C | ISO11359-2 | 2.8E-04 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：-- | ISO11359-2 | 2E-04 | cm/cm/°C |
| Linear coefficient of thermal expansion | MD：-40to23°C | ISO11359-2 | 2.8E-04 | cm/cm/°C |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 2.2E-04 | cm/cm/°C |
| Melting temperature 2 | | ISO11357-3 | 193 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric strength | | IEC60243-1 | 18 | KV/mm |
| Relative permittivity | 100Hz | IEC60250 | 4.80 | |
| Relative permittivity | 1MHz | IEC60250 | 4.70 | |
| Leakage Trace Index | | IEC60112 | 600 | V |
| Dissipation factor | 100Hz | IEC60250 | 0.013 | |
| Dissipation factor | 1MHz | IEC60250 | 0.020 | |
| Surface resistivity | | IEC60093 | 3E+14 | ohms |
| Volume resistivity | | IEC60093 | 4E+12 | ohms·cm |
| elastomer | Test Condition | Test Method | Test Result | Unit |
|---|
| tear strength | 横向流量 | ISO34-1 | 100 | kN/m |
| tear strength | 流量 | ISO34-1 | 100 | kN/m |
| film | Test Condition | Test Method | Test Result | Unit |
|---|
| WaterVaporTransmission Rate | 23°C,85%RH,25µm | DIS15106-1/-2 | 900 | g/m²/24hr |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | NoBreak | |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | NoBreak | |
| Charpy Notched Impact Strength | -40°C | ISO179/1eA | NoBreak | |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | NoBreak | |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | NoBreak | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | NoBreak | |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | NoBreak | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore hardness | 邵氏D | ISO868 | 37 | |
| Shore hardness | 邵氏D,15秒 | ISO868 | 33 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| FMVSS flammability | | FMVSS302 | B | |
| Burning rate 3 | 1.00mm | ISO3795 | <100 | mm/min |
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| UL flame retardant rating | 3.0mm | UL94 | HB | |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
| UL flame retardant rating | 3.0mm | IEC60695-11-10,-20 | HB | |
| Extreme Oxygen Index | | ISO4589-2 | 20 | % |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| EmissionofOrganicCompounds | | VDA277 | 10.0 | µgC/g |
| Odor | | VDA270 | 4.00 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.