TPE Hytrel® 4069 DUPONT USA

221

Unit Price:
$12270 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
16MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Aging resistance Low temperature resistanc High temperature resistan
Application Areas:Electrical field Electrical appliances Electronic field Automotive sector
Color:--
Grade:Extrusion grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Density/specific gravity		ISO1183	1.11	g/cm³
Melt mass flow rate	220°C/2.16kg	ISO1133	8.5	g/10min
Melt volume flow rate	220°C/2.16kg	ISO1133	8.80	cm3/10min
Shrinkage rate	TD	ISO294-4	0.80	%
Shrinkage rate	Shrinkage rate	MD	ISO294-4	0.80	%
Water absorption rate	23°C,24hr	ISO62	0.70	%
	Water absorption rate	Saturation,23°C,2.00mm	ISO62	0.70	%
	Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO62	0.30	%
MediumDensity			1.10	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ISO527-2	45.0	Mpa
Tensile stress	Break	ISO527-2	29.0	Mpa
	Tensile stress	10%Strain	ISO527-2	3.20	Mpa
	Tensile stress	Tensile stress	50%Strain	ISO527-2	6.70	Mpa
Tensile strain	Break	ISO527-2	>300	%
Nominal tensile fracture strain		ISO527-2	800	%
Bending modulus		ISO178	45.0	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Brittle temperature		ISO974	-96.0	°C
Glass transition temperature 2		ISO11357-2	-50.0	°C
Linear coefficient of thermal expansion	TD：-40to23°C	ISO11359-2	2.8E-04	cm/cm/°C
	Linear coefficient of thermal expansion	TD：--	ISO11359-2	2E-04	cm/cm/°C
		Linear coefficient of thermal expansion	MD：-40to23°C	ISO11359-2	2.8E-04	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：--	ISO11359-2	2.2E-04	cm/cm/°C
Melting temperature 2		ISO11357-3	193	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative permittivity	100Hz	IEC60250	4.80
Relative permittivity	Relative permittivity	1MHz	IEC60250	4.70
Dielectric strength		IEC60243-1	18	KV/mm
Volume resistivity		IEC60093	4E+12	ohms·cm
Surface resistivity		IEC60093	3E+14	ohms
Dissipation factor	100Hz	IEC60250	0.013
Dissipation factor	Dissipation factor	1MHz	IEC60250	0.020
Leakage Trace Index		IEC60112	600	V

elastomer	Test Condition	Test Method	Test Result	Unit
tear strength	Across Flow	ISO34-1	100	kN/m
tear strength	tear strength	流量	ISO34-1	100	kN/m

film	Test Condition	Test Method	Test Result	Unit
WaterVaporTransmission Rate	23°C,85%RH,25µm	DIS15106-1/-2	900	g/m²/24hr

Impact performance	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-40°C	ISO179/1eA	NoBreak
	Charpy Notched Impact Strength	-30°C	ISO179/1eA	NoBreak
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	NoBreak
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	NoBreak
Impact strength of cantilever beam gap	-40°C	ISO180/1A	NoBreak
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO180/1A	NoBreak

hardness	Test Condition	Test Method	Test Result	Unit
Shore hardness	Shore D	ISO868	37
Shore hardness	Shore hardness	Shore D,15sec	ISO868	33

flammability	Test Condition	Test Method	Test Result	Unit
Burning rate 3	1.00mm	ISO3795	<100	mm/min
UL flame retardant rating	1.5mm	UL94	HB
	UL flame retardant rating	3.0mm	UL94	HB
		UL flame retardant rating	1.5mm	IEC60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	3.0mm	IEC60695-11-10,-20	HB
Extreme Oxygen Index		ISO4589-2	20	%
FMVSS flammability		FMVSS302	B

Supplementary Information	Test Condition	Test Method	Test Result	Unit
Odor		VDA270	4.00
EmissionofOrganicCompounds		VDA277	10.0	µgC/g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.