ABS/PC CYCOLOY™ XCY630L-BK1566U SABIC INNOVATIVE US
431
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 260°C/5.0kg | ASTMD1238 | 26 | g/10min |
| Melt volume flow rate | 260°C/5.0kg | ISO1133 | 22.0 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| TD：3.20mm | 内部方法 | 0.50to0.70 | % | |
| Water absorption rate | 饱和,23°C | ISO62 | 0.40 | % |
| 平衡,23°C,50%RH | ISO62 | 0.15 | % | |
| MeltViscosity | 260°C,1500sec^-1 | ISO11443 | 170 | Pa·s |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | 屈服 | ISO527-2/50 | 54.0 | Mpa |
| Tensile strength 3 | 断裂 | ASTMD638 | 53.0 | Mpa |
| Tensile stress | 断裂 | ISO527-2/50 | 53.0 | Mpa |
| Tensile modulus 2 | ASTMD638 | 2300 | Mpa | |
| Tensile modulus | ISO527-2/1 | 2250 | Mpa | |
| Tensile strength 3 | 屈服 | ASTMD638 | 54.0 | Mpa |
| Elongation rate 3 | 屈服 | ASTMD638 | 4.5 | % |
| Tensile strain | 屈服 | ISO527-2/50 | 4.5 | % |
| Elongation rate 4 | 断裂 | ASTMD638 | 120 | % |
| Tensile strain | 断裂 | ISO527-2/50 | 120 | % |
| Bending modulus 4 | 50.0mm跨距 | ASTMD790 | 2300 | Mpa |
| Bending modulus 5 | ISO178 | 2200 | Mpa | |
| Bending strength 5,6 | ISO178 | 82.0 | Mpa | |
| Bending strength 4 | 屈服,50.0mm跨距 | ASTMD790 | 89.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | -- | ISO306/B50 | 126 | °C |
| -- | ISO306/B120 | 127 | °C | |
| BallPressure Test | 75°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7E-05 | cm/cm/°C |
| MD：-40到40°C | ISO11359-2 | 8E-05 | cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 7E-05 | cm/cm/°C | |
| TD：-40到40°C | ISO11359-2 | 8E-05 | cm/cm/°C | |
| thermal conductivity | ISO8302 | 0.20 | W/m/K | |
| Hot deformation temperature 9 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 126 | °C |
| Hot deformation temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 107 | °C |
| Hot deformation temperature 9 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 105 | °C |
| Vicat softening temperature | ASTMD152510 | 126 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | 0.800mm,在油中 | IEC60243-1 | 35 | KV/mm |
| 1.60mm,在油中 | IEC60243-1 | 25 | KV/mm | |
| 3.20mm,在油中 | IEC60243-1 | 17 | KV/mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 7 | -30°C | ISO179/1eA | 30 | kJ/m² |
| 23°C | ISO179/1eA | 65 | kJ/m² | |
| Suspended wall beam gap impact strength 8 | -30°C | ISO180/1A | 30 | kJ/m² |
| 23°C | ISO180/1A | 65 | kJ/m² | |
| Dart impact equipped with measuring instruments | -30°C,TotalEnergy | ASTMD3763 | 67.0 | J |
| 23°C,TotalEnergy | ASTMD3763 | 55.0 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.