ABS/PC CYCOLOY™ XCY630L-BK1566U SABIC INNOVATIVE US
126
- Unit Price:
- $4908 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 260°C/5.0kg | ASTMD1238 | 26 | g/10min |
| Melt volume flow rate | 260°C/5.0kg | ISO1133 | 22.0 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| TD：3.20mm | 内部方法 | 0.50to0.70 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.40 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % | |
| MeltViscosity | 260°C,1500sec^-1 | ISO11443 | 170 | Pa·s |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Yield | ISO527-2/50 | 54.0 | Mpa |
| Tensile strength 3 | Break | ASTMD638 | 53.0 | Mpa |
| Tensile stress | Break | ISO527-2/50 | 53.0 | Mpa |
| Tensile modulus 2 | ASTMD638 | 2300 | Mpa | |
| Tensile modulus | ISO527-2/1 | 2250 | Mpa | |
| Tensile strength 3 | Yield | ASTMD638 | 54.0 | Mpa |
| Elongation rate 3 | Yield | ASTMD638 | 4.5 | % |
| Tensile strain | Yield | ISO527-2/50 | 4.5 | % |
| Elongation rate 4 | Break | ASTMD638 | 120 | % |
| Tensile strain | Break | ISO527-2/50 | 120 | % |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 2300 | Mpa |
| Bending modulus 5 | ISO178 | 2200 | Mpa | |
| Bending strength 5,6 | ISO178 | 82.0 | Mpa | |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 89.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | -- | ISO306/B50 | 126 | °C |
| -- | ISO306/B120 | 127 | °C | |
| BallPressure Test | 75°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 8E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 8E-05 | cm/cm/°C | |
| thermal conductivity | ISO8302 | 0.20 | W/m/K | |
| Hot deformation temperature 9 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 126 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 107 | °C |
| Hot deformation temperature 9 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 105 | °C |
| Vicat softening temperature | ASTMD152510 | 126 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | 0.800mm,in Oil | IEC60243-1 | 35 | KV/mm |
| 1.60mm,in Oil | IEC60243-1 | 25 | KV/mm | |
| 3.20mm,in Oil | IEC60243-1 | 17 | KV/mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 7 | -30°C | ISO179/1eA | 30 | kJ/m² |
| 23°C | ISO179/1eA | 65 | kJ/m² | |
| Suspended wall beam gap impact strength 8 | -30°C | ISO180/1A | 30 | kJ/m² |
| 23°C | ISO180/1A | 65 | kJ/m² | |
| Dart impact equipped with measuring instruments | -30°C,TotalEnergy | ASTMD3763 | 67.0 | J |
| 23°C,TotalEnergy | ASTMD3763 | 55.0 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.