Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | 流动 | ASTM D955 | 0.22 | % |
| Shrinkage rate | 横向流动 | ASTM D955 | 0.66 | % |
| Water absorption rate | 饱和 | ASTM D570 | 0.020 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| elongation | 断裂 | ASTM D638 | 4.3 | % |
| Bending modulus | 23°C | ASTM D790 | 13500 | Mpa |
| bending strength | 23°C | ASTM D790 | 134 | Mpa |
| shear strength | | ASTM D732 | 50.0 | Mpa |
| Poisson's ratio | | ASTM E132 | 0.39 | |
| Tensile strength | | ASTM D638 | 126 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear coefficient of thermal expansion | 流动 : 50 到 150°C | ASTM D696 | 1.1E-5 | cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 : 50 到 150°C | ASTM D696 | 6.5E-5 | cm/cm/°C |
| Thermal deformation temperature under load | 1.8 MPa, 未退火 | ASTM D648 | 284 | °C |
| RTI | 3.2 mm | UL 746 | 240 | °C |
| RTI Imp | 3.2 mm | UL 746 | 200 | °C |
| RTI Elec | 3.2 mm | UL 746 | 220 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric constant | 1 kHz | ASTM D150 | 4.30 | |
| Dielectric constant | 1 MHz | ASTM D150 | 3.90 | |
| Arc resistance | | ASTM D495 | 130 | sec |
| Volume resistivity | | ASTM D257 | 1.0E+15 | ohms·cm |
| Dissipation factor | 1 kHz | ASTM D150 | 0.019 | |
| Dissipation factor | 1 MHz | ASTM D150 | 0.028 | |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | 165 | V |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Injection pressure | | | 78.0 到 157 | Mpa |
| Suggested maximum recycled material ratio | | | 30 | % |
| Injection speed | | | 中等偏快 | |
| drying time | | | 3.0 | hr |
| Temperature at the rear of the barrel | | | 300 到 320 | °C |
| Temperature in the middle of the barrel | | | 320 到 350 | °C |
| Temperature at the front of the material cylinder | | | 340 到 370 | °C |
| Spray nozzle temperature | | | 340 到 370 | °C |
| Back pressure | | | 0.980 到 4.90 | Mpa |
| Screw speed | | | 50 到 100 | rpm |
| drying temperature | | | 120 到 150 | °C |
| Mold temperature | | | 70 到 160 | °C |
| Maintain pressure | | | 20.0 到 39.0 | Mpa |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Non notched cantilever beam impact | 6.40 mm | ASTM D256 | 280 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R 级 | ASTM D785 | 103 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Extreme Oxygen Index | | ASTM D2863 | 46 | % |
| UL flame retardant rating | 0.30 mm | UL 94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.