LCP SUMIKASUPER® E6810LHF-BZ SUMITOMO JAPAN
160
Unit Price:$8300 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 80MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low warpage Good forming performance Glass fiber reinforced
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | 流动 | ASTM D955 | 0.22 | % |
| 横向流动 | ASTM D955 | 0.66 | % | |
| 吸水率 | 饱和 | ASTM D570 | 0.020 | % |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 抗张强度 | ASTM D638 | 126 | Mpa | |
| 伸长率 | 断裂 | ASTM D638 | 4.3 | % |
| 弯曲模量 | 23°C | ASTM D790 | 13500 | Mpa |
| 弯曲强度 | 23°C | ASTM D790 | 134 | Mpa |
| 剪切强度 | ASTM D732 | 50.0 | Mpa | |
| 泊松比 | ASTM E132 | 0.39 |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 载荷下热变形温度 | 1.8 MPa, 未退火 | ASTM D648 | 284 | °C |
| 线形热膨胀系数 | 流动 : 50 到 150°C | ASTM D696 | 1.1E-5 | cm/cm/°C |
| 横向 : 50 到 150°C | ASTM D696 | 6.5E-5 | cm/cm/°C | |
| RTI Elec | 3.2 mm | UL 746 | 220 | °C |
| RTI Imp | 3.2 mm | UL 746 | 200 | °C |
| RTI | 3.2 mm | UL 746 | 240 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 体积电阻率 | ASTM D257 | 1.0E+15 | ohms·cm | |
| 介电常数 | 1 kHz | ASTM D150 | 4.30 | |
| 1 MHz | ASTM D150 | 3.90 | ||
| 耗散因数 | 1 kHz | ASTM D150 | 0.019 | |
| 1 MHz | ASTM D150 | 0.028 | ||
| 耐电弧性 | ASTM D495 | 130 | sec | |
| 相比耐漏电起痕指数(CTI) | UL 746 | 165 | V |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥温度 | 120 到 150 | °C | ||
| 干燥时间 | 3.0 | hr | ||
| 建议的最大回制料比例 | 30 | % | ||
| 料筒后部温度 | 300 到 320 | °C | ||
| 料筒中部温度 | 320 到 350 | °C | ||
| 料筒前部温度 | 340 到 370 | °C | ||
| 射嘴温度 | 340 到 370 | °C | ||
| 模具温度 | 70 到 160 | °C | ||
| 注塑压力 | 78.0 到 157 | Mpa | ||
| 注射速度 | 中等偏快 | |||
| 保压 | 20.0 到 39.0 | Mpa | ||
| 背压 | 0.980 到 4.90 | Mpa | ||
| 螺杆转速 | 50 到 100 | rpm |
| 冲击性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 无缺口悬臂梁冲击 | 6.40 mm | ASTM D256 | 280 | J/m |
| 硬度 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 洛氏硬度 | R 级 | ASTM D785 | 103 |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL 阻燃等级 | 0.30 mm | UL 94 | V-0 | |
| 极限氧指数 | ASTM D2863 | 46 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.