ABS/PC CYCOLAC™ DL200H-BK4051 SABIC INNOVATIVE NANSHA

616

Properties:
High heat resistance
Hydrolysis resistance
Usages:
Electronic and electrical
Automotive components
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Melt mass flow rate	260°C/5.0kg	ASTMD1238	25	g/10min
Melt mass flow rate	Melt mass flow rate	220°C/10.0kg	ISO1133	9.0	g/10min

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus 2		ASTMD638	2330	Mpa
Tensile modulus		ISO527-2/1	2350	Mpa
Tensile strength 3	屈服	ASTMD638	47.0	Mpa
Tensile stress	屈服	ISO527-2/50	49.0	Mpa
Tensile stress	Tensile stress	断裂	ISO527-2/50	40.0	Mpa
Tensile strain	屈服	ISO527-2/50	3.9	%
Elongation rate 4	断裂	ASTMD638	70	%
Tensile strain	断裂	ISO527-2/50	75	%
Bending modulus 4	50.0mm跨距	ASTMD790	2200	Mpa
Bending modulus 5		ISO178	2100	Mpa
Bending strength 5,6		ISO178	75.0	Mpa
Bending strength 4	屈服,50.0mm跨距	ASTMD790	77.0	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,未退火,3.20mm	ASTMD648	118	°C
Hot deformation temperature 9	0.45MPa,Unannealed,64.0mmSpan	ISO75-2/Bf	120	°C
Hot deformation temperature	1.8MPa,未退火,3.20mm	ASTMD648	96.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,未退火,6.40mm	ASTMD648	101	°C
Hot deformation temperature 9	1.8MPa,Unannealed,64.0mmSpan	ISO75-2/Af	96.0	°C
Vicat softening temperature	--	ISO306/B50	112	°C
Vicat softening temperature	Vicat softening temperature	--	ISO306/B120	114	°C

Impact performance	Test Condition	Test Method	Test Result	Unit
Suspended wall beam gap impact strength 8	23°C	ISO180/1A	56	kJ/m²
Impact strength of simply supported beam gap 7	-30°C	ISO179/1eA	30	kJ/m²
Impact strength of simply supported beam gap 7	Impact strength of simply supported beam gap 7	23°C	ISO179/1eA	65	kJ/m²
Suspended wall beam gap impact strength 8	-40°C	ISO180/1A	21	kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.