Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS/PC DL200H-BK4051 SABIC INNOVATIVE NANSHA
CYCOLAC™
Electronic and electrical、Automotive components
High heat resistance、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ABS/PC/SABIC INNOVATIVE NANSHA/DL200H-BK4051
Melt mass flow rate
260°C/5.0kg
ASTMD1238
g/10min
2
Melt mass flow rate
220°C/10.0kg
ISO1133
g/10min
9
Mechanical performance
Test Condition
Test Method
Unit
ABS/PC/SABIC INNOVATIVE NANSHA/DL200H-BK4051
Tensile strength 3
屈服
ASTMD638
Mpa
4
Tensile modulus
ISO527-2/1
Mpa
2
Tensile modulus 2
ASTMD638
Mpa
2
Tensile strain
断裂
ISO527-2/50
%
7
Tensile strain
屈服
ISO527-2/50
%
3
Tensile stress
屈服
ISO527-2/50
Mpa
4
Tensile stress
断裂
ISO527-2/50
Mpa
4
Elongation rate 4
断裂
ASTMD638
%
7
Bending modulus 4
50.0mm跨距
ASTMD790
Mpa
2
Bending modulus 5
ISO178
Mpa
2
Bending strength 4
屈服,50.0mm跨距
ASTMD790
Mpa
7
Bending strength 5,6
ISO178
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
ABS/PC/SABIC INNOVATIVE NANSHA/DL200H-BK4051
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
9
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
1
Hot deformation temperature 9
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
9
Hot deformation temperature 9
0.45MPa,Unannealed,64.0mmSpan
ISO75-2/Bf
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Impact performance
Test Condition
Test Method
Unit
ABS/PC/SABIC INNOVATIVE NANSHA/DL200H-BK4051
Impact strength of simply supported beam gap 7
-30°C
ISO179/1eA
kJ/m²
3
Impact strength of simply supported beam gap 7
23°C
ISO179/1eA
kJ/m²
6
Suspended wall beam gap impact strength 8
-40°C
ISO180/1A
kJ/m²
2
Suspended wall beam gap impact strength 8
23°C
ISO180/1A
kJ/m²
5