PBT VALOX™ ENH4550 SABIC INNOVATIVE US
305
- Properties:High rigidityGlass fiber reinforced
- Usages:Electrical applicationsAutomotive Applications
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：--2 | 内部方法 | 0.10to0.50 | % |
| MD：3.20mm | 内部方法 | 0.10to0.50 | % | |
| TD：--2 | 内部方法 | 0.60to1.2 | % | |
| TD：3.20mm | 内部方法 | 0.50to1.1 | % | |
| Water absorption rate | 饱和,23°C | ISO62 | 0.23 | % |
| 平衡,23°C,50%RH | ISO62 | 0.060 | % | |
| Melt mass flow rate | 250°C/5.0kg | ASTMD1238 | 27 | g/10min |
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 20.0 | cm3/10min |
| MeltViscosity | 250°C,1500sec^-1 | ISO11443 | 210 | Pa·s |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | 屈服 | ISO527-2/5 | 112 | Mpa |
| 断裂 | ISO527-2/5 | 112 | Mpa | |
| Tensile strain | 屈服 | ISO527-2/5 | 2.0 | % |
| 断裂 | ISO527-2/5 | 2.0 | % | |
| Tensile modulus | ISO527-2/1 | 10400 | Mpa | |
| Elongation rate 4 | 断裂 | ASTMD638 | 2.0 | % |
| 屈服 | ASTMD638 | 2.0 | % | |
| Bending modulus 5 | 50.0mmSpan | ASTMD790 | 9100 | Mpa |
| FlexuralStrength5 | Yield,50.0mmSpan | ASTMD790 | 161 | Mpa |
| Tensile strength 4 | 屈服 | ASTMD638 | 105 | Mpa |
| Bending strength 6,7 | ISO178 | 170 | Mpa | |
| Tensile modulus 3 | ASTMD638 | 9900 | Mpa | |
| Tensile strength 4 | Break | ASTMD638 | 105 | Mpa |
| Bending modulus 6 | ISO178 | 9400 | Mpa | |
| Fracture bending strain 8 | ISO178 | 2.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature 11 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 219 | °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 201 | °C | |
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| Hot deformation temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 216 | °C |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 204 | °C | |
| Vicat softening temperature | -- | ASTMD152512 | 215 | °C |
| -- | ASTMD152513 | 202 | °C | |
| -- | ISO306/A50 | 219 | °C | |
| -- | ISO306/B50 | 206 | °C | |
| -- | ISO306/B120 | 206 | °C | |
| RTIElec | UL746 | 130 | °C | |
| Evolution Calendar intelligent importer | UL746 | 140 | °C | |
| RTIStr | UL746 | 140 | °C | |
| Linear coefficient of thermal expansion | TD：-40to40°C | ASTME831 | 7.1E-05 | cm/cm/°C |
| TD：-40to150°C | ASTME831 | 7.7E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 7.6E-05 | cm/cm/°C | |
| TD：23到80°C | ISO11359-2 | 9.1E-05 | cm/cm/°C | |
| MD：-40to40°C | ASTME831 | 2.7E-05 | cm/cm/°C | |
| MD：-40to150°C | ASTME831 | 2.2E-05 | cm/cm/°C | |
| MD：-40to40°C | ISO11359-2 | 3E-05 | cm/cm/°C | |
| MD：23到80°C | ISO11359-2 | 2.2E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 3.20mm,在油中 | ASTMD149 | 21 | KV/mm |
| 3.20mm,inAir | ASTMD149 | 21 | KV/mm | |
| Compared to the anti leakage trace index | CTI | UL746 | PLC2 | |
| Leakage Trace Index | IEC60112 | 300 | V | |
| Volume resistivity | ASTMD257 | 1.0E+15to1.0E+16 | ohms·cm | |
| IEC60093 | 1.0E+15to1.0E+16 | ohms·cm | ||
| Arc resistance 14 | ASTMD495 | PLC6 | ||
| Hot wire ignition | HWI | UL746 | PLC0 | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC0 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Suspended wall beam gap impact strength 10 | -30°C | ISO180/1A | 7.0 | kJ/m² |
| 23°C | ISO180/1A | 7.0 | kJ/m² | |
| Unscented Izod Impact Strength 10 | -30°C | ISO180/1U | 29 | kJ/m² |
| 23°C | ISO180/1U | 33 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/2U | 33 | kJ/m² |
| 23°C | ISO179/2U | 36 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 6.50 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot filament ignition temperature | 0.8mm | IEC60695-2-13 | 775 | °C |
| 3.0mm15 | IEC60695-2-13 | 775 | °C | |
| UL flame retardant rating | 0.75mm | UL94 | V-0 | |
| 3.0mm | UL94 | 5VA | ||
| Burning wire flammability index | 0.75mm | IEC60695-2-12 | 960 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.