PBT VALOX™ ENH4550 SABIC INNOVATIVE US
119
- Unit Price:
- $5013 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 25MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity Glass fiber reinforced
- Application Areas:Electrical applications Automotive Applications
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：--2 | 内部方法 | 0.10to0.50 | % |
| MD：3.20mm | 内部方法 | 0.10to0.50 | % | |
| TD：--2 | 内部方法 | 0.60to1.2 | % | |
| TD：3.20mm | 内部方法 | 0.50to1.1 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.23 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.060 | % | |
| Melt mass flow rate | 250°C/5.0kg | ASTMD1238 | 27 | g/10min |
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 20.0 | cm3/10min |
| MeltViscosity | 250°C,1500sec^-1 | ISO11443 | 210 | Pa·s |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Yield | ISO527-2/5 | 112 | Mpa |
| Break | ISO527-2/5 | 112 | Mpa | |
| Tensile strain | Yield | ISO527-2/5 | 2.0 | % |
| Break | ISO527-2/5 | 2.0 | % | |
| Tensile modulus | ISO527-2/1 | 10400 | Mpa | |
| Elongation rate 4 | Break | ASTMD638 | 2.0 | % |
| Yield | ASTMD638 | 2.0 | % | |
| Bending modulus 5 | 50.0mmSpan | ASTMD790 | 9100 | Mpa |
| FlexuralStrength5 | Yield,50.0mmSpan | ASTMD790 | 161 | Mpa |
| Tensile strength 4 | Yield | ASTMD638 | 105 | Mpa |
| Bending strength 6,7 | ISO178 | 170 | Mpa | |
| Tensile modulus 3 | ASTMD638 | 9900 | Mpa | |
| Tensile strength 4 | Break | ASTMD638 | 105 | Mpa |
| Bending modulus 6 | ISO178 | 9400 | Mpa | |
| Fracture bending strain 8 | ISO178 | 2.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature 11 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 219 | °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 201 | °C | |
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 216 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 204 | °C | |
| Vicat softening temperature | -- | ASTMD152512 | 215 | °C |
| -- | ASTMD152513 | 202 | °C | |
| -- | ISO306/A50 | 219 | °C | |
| -- | ISO306/B50 | 206 | °C | |
| -- | ISO306/B120 | 206 | °C | |
| RTIElec | UL746 | 130 | °C | |
| Evolution Calendar intelligent importer | UL746 | 140 | °C | |
| RTIStr | UL746 | 140 | °C | |
| Linear coefficient of thermal expansion | TD：-40to40°C | ASTME831 | 7.1E-05 | cm/cm/°C |
| TD：-40to150°C | ASTME831 | 7.7E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 7.6E-05 | cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 9.1E-05 | cm/cm/°C | |
| MD：-40to40°C | ASTME831 | 2.7E-05 | cm/cm/°C | |
| MD：-40to150°C | ASTME831 | 2.2E-05 | cm/cm/°C | |
| MD：-40to40°C | ISO11359-2 | 3E-05 | cm/cm/°C | |
| MD：23to80°C | ISO11359-2 | 2.2E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 3.20mm,in Oil | ASTMD149 | 21 | KV/mm |
| 3.20mm,inAir | ASTMD149 | 21 | KV/mm | |
| Compared to the anti leakage trace index | CTI | UL746 | PLC2 | |
| Leakage Trace Index | IEC60112 | 300 | V | |
| Volume resistivity | ASTMD257 | 1.0E+15to1.0E+16 | ohms·cm | |
| IEC60093 | 1.0E+15to1.0E+16 | ohms·cm | ||
| Arc resistance 14 | ASTMD495 | PLC6 | ||
| Hot wire ignition | HWI | UL746 | PLC0 | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC0 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Suspended wall beam gap impact strength 10 | -30°C | ISO180/1A | 7.0 | kJ/m² |
| 23°C | ISO180/1A | 7.0 | kJ/m² | |
| Unscented Izod Impact Strength 10 | -30°C | ISO180/1U | 29 | kJ/m² |
| 23°C | ISO180/1U | 33 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/2U | 33 | kJ/m² |
| 23°C | ISO179/2U | 36 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 6.50 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot filament ignition temperature | 0.8mm | IEC60695-2-13 | 775 | °C |
| 3.0mm15 | IEC60695-2-13 | 775 | °C | |
| UL flame retardant rating | 0.75mm | UL94 | V-0 | |
| 3.0mm | UL94 | 5VA | ||
| Burning wire flammability index | 0.75mm | IEC60695-2-12 | 960 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.